In order to solve the problem that the metal colored glaze is easy to leach in the conventional tea making method, which will affect the health of the body, the invention proposes a making method of raking flower tea which can effectively reduce the leaching of lead, cadmium and other harmful substances in the glaze. In order to achieve the above purpose, the technical scheme adopted in the invention is a production method of raking flower tea utensil, which includes the following steps: S1: making the blank, making the shape of the utensil; S2: putting the utensil into the kiln for plain burning, burning off the moisture in the blank to ensure that it is not easy to break; S3: manually coloring the utensil with blue and white material; S4: using the pen, knife or embroidery needle tools for the utensil Sculpture and decoration; S5: glaze the decorated objects; S6: load the glazed objects into the kiln and burn them; S7: after burning, cool them for 8-10 hours before picking them out of the kiln.
【技术实现步骤摘要】
一种耙花茶器的制作方法
本专利技术创造属于器皿制作方法领域，具体涉及了一种耙花茶器的制作方法。
技术介绍
现有技术方案是在烧成的瓷器上再覆盖一层色釉，再对其进行耙花绘制。现有的技术制作出来的成品率高，且容易操作。但是其缺点在于，成瓷上覆盖一层釉，经烤花烧制，其坯体原釉不能融解，故附着在瓷器上。金属色釉，重金属容易浸出，会影响身体健康，不适作用日常使用的茶器和食器制品当中。
技术实现思路
为了解决上述存在的常规的茶器制作方法中金属色釉容易浸出会影响到身体健康的问题，本专利技术创造提出了一种可以有效减少釉料中铅、镉等有害物质的浸出的耙花茶器的制作方法。为了实现上述目的，本专利技术创造所采用的技术方案是，一种耙花茶器的制作方法，包括以下步骤：S1：拉坯制作，制作器物的造型；S2：将器物入烤花窑素烧，烧除坯胎中的水分确保不易破碎；S3：对器物用青花料手工上色；S4：对器物用笔、刀具或绣花针类工具进行雕刻、装饰；S5：对装饰好的器物进行罩釉；S6：将施釉好的器物进行装窑入烧；S7：烧炼完成，进行8-...
【技术保护点】
1.一种耙花茶器的制作方法，其特征在于，包括以下步骤：/nS1：拉坯制作，制作器物的造型；/nS2：将器物入烤花窑素烧，烧除坯胎中的水分确保不易破碎；/nS3：对器物用青花料手工上色；/nS4：对器物用笔、刀具或绣花针类工具进行雕刻、装饰；/nS5：对装饰好的器物进行罩釉；/nS6：将施釉好的器物进行装窑入烧；/nS7：烧炼完成，进行8-10小时的冷却方能将器物拣出窖炉。/n
【技术特征摘要】
1.一种耙花茶器的制作方法，其特征在于，包括以下步骤：
S1：拉坯制作，制作器物的造型；
S2：将器物入烤花窑素烧，烧除坯胎中的水分确保不易破碎；
S3：对器物用青花料手工上色；
S4：对器物用笔、刀具或绣花针类工具进行雕刻、装饰；
S5：对装饰好的器物进行...