The invention discloses a processing technology of colour resin crystal for decoration, which is made of resin, alcohol, water and water-soluble dyes. The colour mixture consisting of alcohol, water and water-soluble dyes is added with macromolecule water absorbent resin, which is soaked, dried and dried. It can be used as indoor decoration or tourist handicraft, and can insert various flowers or replace clay to make box scenery and lamp. Decoration, etc. The invention has all decorative effects of crystal mud. The volume will not shrink and shrink, and will not sink. Keep the crystal appearance for long-term appreciation.
【技术实现步骤摘要】
一种装饰用彩色树脂水晶的加工工艺
本专利技术属于生活装饰品的制作方法,特别是一种装饰用彩色树脂水晶的加工工艺。
技术介绍
目前市面流行的多彩育花水晶泥,都是利用高分子吸水树脂吸收水分后膨涨而成的似水晶状的物体,用于栽种阴生植物和水生花卉,但水晶泥的缺陷是:1、栽种的花卉过于单调,只局限于阴生植物和水生花卉。2、水晶泥的水分不断蒸发导致失水,体积不断缩小,造成水晶泥下陷,需要经常补加水晶泥。3、水晶泥装在透明容器内,初期显露水晶状态,但过一段时间后大部分水晶泥连成一片,类似果冻一样,失去水晶外观,无欣赏价值。
技术实现思路
本专利技术的目的是提供一种装饰用彩色树脂水晶的加工工艺,在由醇、水和水溶性染料组成的彩色混合液中加入高分子吸水树脂,经浸泡、沥干、烘干而成,可作室内装饰品或制作旅游工艺品,可插各种仿真花或代替泥土制作盒景及作灯饰等。本专利技术由高分子吸水树脂、醇、水和水溶性染料制成,在10-60公斤的水中加入0.01-0.5公斤的水溶性染料搅拌至完全溶解,再加入40-90公斤醇,搅拌混合得彩色混合液;然后称取0.5-5公斤的高分子吸水树脂投入彩色混合液中浸泡,高分子吸水树脂膨涨成水晶状软固体,再沥干多余的彩色混合液,摊开风干或用烘干机控制温度在40-60℃烘干至水分含量在5-15%之间,即成。本专利技术具有水晶泥的一切装饰效果。体积不会收缩变小,不会下陷。长期保持水晶状外观供欣赏。具体实施方式实施例1在10公斤的自来水中加入0.08公斤水溶性染料酸性金黄G搅拌至完全溶解,再加入86公斤乙二醇,搅拌混合得彩色混合液;然后称取3.92公斤的高分子吸水树脂投入彩色混合 ...
【技术保护点】
1.一种装饰用彩色树脂水晶的加工工艺,由高分子吸水树脂、醇、水和水溶性染料制成,其特征是在10‑60公斤的水中加入0.01‑0.5公斤的水溶性染料搅拌至完全溶解,再加入40‑90公斤醇,搅拌混合得彩色混合液;然后称取0.5 ‑5公斤的高分子吸水树脂投入彩色混合液中浸泡,高分子吸水树脂膨涨成水晶状软固体,再沥干多余的彩色混合液,摊开风干或用烘干机控制温度在40‑60℃烘干至水分含量在5‑15%之间,即成。
【技术特征摘要】
1.一种装饰用彩色树脂水晶的加工工艺,由高分子吸水树脂、醇、水和水溶性染料制成,其特征是在10-60公斤的水中加入0.01-0.5公斤的水溶性染料搅拌至完全溶解,再加入40-90公斤醇,搅拌混合得彩色混合液;然后称取0.5-5公斤的高分子吸水树脂投入彩色混合液中浸泡,高分子吸水树脂膨涨成水晶状软固体,再沥干多余的彩色混合液,摊开风干或用...