一种宝塔盐的制备方法技术

本发明专利技术涉及盐业化工制备领域，旨在提供一种宝塔盐的制备方法。提供一种宝塔盐的制备方法，包括以下步骤：向预热后的精卤中加入占其质量0.01～0.5％的葡萄糖，混合均匀；然后在40～90℃条件下结晶12h～24h，制得宝塔盐产品。与现有技术相比，本发明专利技术制备方法简单易行、方便控制。生产成本低廉，具有广阔的市场前景。本发明专利技术制备得到的食盐，其防结块性能优于普通食盐，是一种新的功能性盐。

A preparation method of pagoda salt

The invention relates to the field of salt industrial chemical preparation, aiming at providing a preparation method of pagoda salt. A preparation method of pagoda salt is provided, which includes the following steps: adding 0.01-0.5% glucose to the preheated brine, mixing evenly, and then crystallizing at 40-90 (?) C for 12-24 h to produce pagoda salt products. Compared with the prior art, the preparation method of the invention is simple, feasible and convenient to control. The production cost is low, and it has broad market prospects. The salt prepared by the invention has better anti-caking performance than common salt, and is a new functional salt.

【技术实现步骤摘要】
一种宝塔盐的制备方法
本专利技术属于盐业化工制备领域，具体涉及一种宝塔盐的制备方法。
技术介绍
盐的用途广泛，是重要的基本化工原料，但价格低廉，附加值不高。目前，一般盐的结晶形状均为正六面体，且盐的粒度比较小，不能完全满足客户的需求。若能通过改变常规氯化钠晶体的晶形或结构可获得各类功能型盐，与现代社会的发展是相适应的。我国目前特殊用盐的消费比例低于国外平均水平，离发达国家的差距更远，加强特殊用盐的品种开发，促进其消费市场的发展，这有助于增加国民经济的发展。宝塔盐作为一种新型的盐产品，是一种新型的特殊用盐，它不仅具备精制盐的所有特点，而且还是一种新的功能性盐。本产品比表面积大，形似金字塔，因此取名为宝塔盐，现在还没有成熟的宝塔盐制备方法。
技术实现思路
本专利技术要解决的技术问题是，克服现有技术中的不足，提供一种宝塔盐的制备方法。为解决技术问题，本专利技术的解决方案是：提供一种宝塔盐的制备方法，包括以下步骤：向预热后的精卤中加入占其质量0.01～0.5％的葡萄糖，混合均匀；然后在40～90℃条件下结晶12h～24h，制得宝塔盐产品。本专利技术中，所述预热是在卤水预热器中进行，预热温度与结晶本文档来自技高网...

【技术保护点】
1.一种宝塔盐的制备方法，其特征在于，包括以下步骤：向预热后的精卤中加入占其质量0.01～0.5％的葡萄糖，混合均匀；然后在40～90℃条件下结晶12～24h，制得宝塔盐产品。

【技术特征摘要】
1.一种宝塔盐的制备方法，其特征在于，包括以下步骤：向预热后的精卤中加入占其质量0.01～0.5％的葡萄糖，混合均匀；然后在40～90℃条件下结晶12～24h，制得宝塔盐产品。2.根据权利要求1所述的方法，其特征在于，所述预热是在卤水预热器中进行，预热温度与结晶温度一致。3.根据权利要求1所述的方法，其特征在于，所述结晶是在卤水结晶器中进行的。4.根据权利要求1所述的方法，其特...

【专利技术属性】
技术研发人员：赵国勇，张玲洁，吕刚，王小琳，
申请(专利权)人：浙江大学自贡创新中心，
类型：发明
国别省市：四川,51