The invention discloses a preparation method of boron carbide modified fluororubber composite material, which includes adding boron carbide inorganic filler into fluororubber, making use of organic combination between particles and rubber, and adopting mechanical melt blending method to prepare composite material. At the same time, particles promote vulcanization reaction of rubber to a certain extent, and improve processing fluidity and product reliability of fluororubber. When the content is between 10% and 15%, the composite has good viscoelastic damping mechanism and structural vibration damping mechanism. The preparation method of the boron carbide modified fluororubber composites can effectively improve the thermal degradation temperature of FKM composites and reduce the thermogravimetric loss of the system by adding boron carbide, thereby improving the thermal stability of the composites. The oil absorption rate of the composites in engine oil is the lowest, which shows good oil corrosion resistance.
【技术实现步骤摘要】
一种碳化硼改性氟橡胶复合材料制备方法
本专利技术涉及橡胶
，具体为一种碳化硼改性氟橡胶复合材料制备方法。
技术介绍
随着国家海洋事业的不断发展，船舶的综合性能得到了显著提高，但在振动及噪声控制
的进展仍相对缓慢，减振降噪技术已成为人们亟待解决的关键难题。阻尼材料由于具有减弱机械振动、降低结构噪声的功效，故在减振降噪
中得到了广泛的关注。然而，随着海洋环境的复杂化，传统的橡胶及聚氨酯等阻尼材料已经难以满足人们对性能的特殊需求。
技术实现思路
本专利技术的目的在于提供一种碳化硼改性氟橡胶复合材料制备方法，以解决上述
技术介绍
中提出的现有的改性氟橡胶复合材料减振降噪能力差的问题。为实现上述目的，本专利技术提供如下技术方案，一种碳化硼改性氟橡胶复合材料制备方法，包括通过向氟橡胶中加入碳化硼无机填料，利用颗粒-橡胶之间的有机结合，采用机械熔融共混法制备复合材料，同时颗粒在一定程度上促进了胶料硫化反应的进行，提升了氟橡胶的加工流动性和制品可靠性；当含量介于10%～15%时，复合材料同时具有良好的粘弹性阻尼机制和结构振动阻尼机制。优选的，所述氟橡胶中加入碳化硼无机填...
【技术保护点】
1.一种碳化硼改性氟橡胶复合材料制备方法，包括通过向氟橡胶中加入碳化硼无机填料，利用颗粒‑橡胶之间的有机结合，采用机械熔融共混法制备复合材料，同时颗粒在一定程度上促进了胶料硫化反应的进行，提升了氟橡胶的加工流动性和制品可靠性；当含量介于10%～15%时，复合材料同时具有良好的粘弹性阻尼机制和结构振动阻尼机制。
【技术特征摘要】
1.一种碳化硼改性氟橡胶复合材料制备方法，包括通过向氟橡胶中加入碳化硼无机填料，利用颗粒-橡胶之间的有机结合，采用机械熔融共混法制备复合材料，同时颗粒在一定程度上促进了胶料硫化反应的进行，提升了氟橡胶的加工流动性和制品可靠性；当含量介于10%～15%时，复合材料同时具有良好的粘弹性阻尼机制和结构振动阻尼机制。2.根据权...
【专利技术属性】
技术研发人员：詹浩，
申请(专利权)人：中绿新材料江苏有限公司，
类型：发明
国别省市：江苏,32