A method of reinforcing ultra-fine Aeolian Sand Roadbed with low softening point asphalt emulsion

The invention belongs to the technical field of highway maintenance, in particular to a method for reinforcing the subgrade of ultra-fine aeolian sand with low softening point bitumen emulsion. The invention adopts the asphalt mixture of low softening point, road asphalt, low temperature coal tar pitch or two kinds of asphalt, which is first processed into asphalt emulsion, then diluted and then sprayed on the fine wind blown sand, and then sprayed and turned over. The amount of asphalt emulsion is equivalent to that of asphalt, which should not be lower than 4Kg/m

【技术实现步骤摘要】
一种用低软化点沥青乳液加固超细风积沙路基的方法
本专利技术属于公路维护
，具体涉及一种用低软化点沥青乳液加固超细风积沙路基的方法。
技术介绍
我国西部有广大的沙漠地带，由于常期受到北方强冷空气和大风的侵入，沙漠及周边地区堆积了大量的超细风积沙，随着西部经济的快速发展，也加大了交通等基础设施的投入。修建高等级公路是首选，而修建公路绕不开这些条件恶劣的超细风积沙地带，路基材料用量大，只能就地取材，不得不利用这些超细风积沙作为路基材料，因此，如何加固这些地带的超细风沙层至关重要。风积沙路基的加固处理量非常大，1Km路基约有0.7～0.8万m3，经过风积沙路段通常在50公里以上甚至数百公里，因此，加固处理方法应该简单易行，造价低。
技术实现思路
针对现有技术存在的问题，本专利技术提供一种用低软化点沥青乳液加固超细风积沙路基的方法，目的是通过利用取自风积沙地带的超细沙，对其进行加固处理，使之具有土壤那样的凝聚力，满足路基的要求，同时具有简单易行、造价低的优势。本专利技术的用低软化点沥青乳液加固超细风积沙路基的方法，按照以下步骤进行：(1)将低软化点沥青加工成沥青乳液；(2)将沥青乳液加水稀释本文档来自技高网...

【技术保护点】
1.一种低软化点沥青乳液加固超细风积沙路基的方法，其特征在于按照以下步骤进行：(1)将低软化点沥青加工成沥青乳液；(2)将沥青乳液加水稀释，喷洒在超细风积沙上，边喷边翻动使其混匀，再压实，每层填筑厚度≤80cm；(3)经压实后再按上述方法铺上第二层、第三层……直至达到设定高度；(4)路基每填筑一层，取样检测粘砂率作为施工质量评定依据，对局部未达到加固要求的部位，再辅以水玻璃溶液加固，最终达到路基加固效果。

【技术特征摘要】
1.一种低软化点沥青乳液加固超细风积沙路基的方法，其特征在于按照以下步骤进行：(1)将低软化点沥青加工成沥青乳液；(2)将沥青乳液加水稀释，喷洒在超细风积沙上，边喷边翻动使其混匀，再压实，每层填筑厚度≤80cm；(3)经压实后再按上述方法铺上第二层、第三层……直至达到设定高度；(4)路基每填筑一层，取样检测粘砂率作为施工质量评定依据，对局部未达到加固要求的部位，再辅以水玻璃溶液加固，最终达到路基加固效果。2.根据权利要...