The present invention provides a carbon fibre prepreg based on epoxy resin and its preparation method. The carbon fibre prepreg is formed in two steps: a preg consists of a reinforced fibre matrix, an epoxy resin composition composed of epoxy resin, thermoplastic resin and curing agent, and the reinforced fibre layer is immersed in the epoxy resin composition; a primary preg formed by hot roll method. The preprepreg is prepared by multilayer pressing with the epoxy resin and the epoxy resin soluble thermoplastic resin, which is dissolved in the epoxy resin. Carbon fiber preprepreg obtained by multi-layer pressing can significantly improve the impact resistance and interlaminar toughness of carbon fiber prepreg based on resin.
【技术实现步骤摘要】
一种碳纤维预浸料及其制备方法
本专利技术专利主要涉及以环氧树脂为基体的碳纤维预浸料及其制备方法，所得的碳纤维预浸料主要用作复合材料的增强。由于其采用多层热辊压制的制作工艺，所得成品可显著提高热固性树脂基体碳纤维预浸料在耐撞击性及层间韧性方面的性能。
技术介绍
碳纤维及其复合材料，因其优异的综合性能及高附加值，被人们称作是二十一世纪的“黑色黄金”。在实际应用中，碳纤维常常用作增强纤维，由碳纤维增强的复合材料通常具有高强度、高刚性与轻量化的特性，由此在现代工业中得到广泛利用，如航空航天、汽车、船舶重工以及深海油田等领域。随着全球科技与生产工艺的进步以及应用领域的扩大，对材料性能的要求也越来越高,而以碳纤维为主要增强材料的碳纤维预浸料已经成为当今复合材料增强领域的研究热点。作为被广泛应用于复合材料纤维增强设计与制造工艺的一类中间材料，碳纤维预浸料就是把基体树脂浸渍在碳纤维中制成片状的叠层材料，是一种纤维与树脂通过相应的层叠方式和工艺制备的未达到固化状态前的产品，是碳纤维制品经常使用的半成品。作为复合材料重要的中间材料，预浸料的性能直接影响到复合材料性能的优劣，因此要求碳...
【技术保护点】
1.本专利技术提供一种以环氧树脂为基体的碳纤维预浸料及其制备方法，其特征在于所述碳纤维预浸料包括两部分：一次预浸料包括强化纤维基体、由环氧树脂、热塑性树脂及固化剂组成的环氧树脂组合物（树脂组合物A），并将强化纤维层浸入此环氧树脂组合物中；含有环氧树脂及溶解于环氧树脂的环氧树脂可溶性热塑性树脂组合物（树脂组合物B），通过热辊法将形成的一次预浸料与含有环氧树脂及溶解于环氧树脂的环氧树脂可溶性热塑性树脂组合物（树脂组合物B）多层压制成型得到最终满足性能要求的预浸料。
【技术特征摘要】
1.本发明提供一种以环氧树脂为基体的碳纤维预浸料及其制备方法，其特征在于所述碳纤维预浸料包括两部分：一次预浸料包括强化纤维基体、由环氧树脂、热塑性树脂及固化剂组成的环氧树脂组合物（树脂组合物A），并将强化纤维层浸入此环氧树脂组合物中；含有环氧树脂及溶解于环氧树脂的环氧树脂可溶性热塑性树脂组合物（树脂组合物B），通过热辊法将形成的一次预浸料与含有环氧树脂及溶解于环氧树脂的环氧树脂可溶性热塑性树脂组合物（树脂组合物B）多层压制成型得到最终满足性能要求的预浸料。2.根据权利要求1所述的碳纤维预浸料一次预浸料，其特征在于，一次预浸料包括强化纤维基体、由环氧树脂、热塑性树脂及固化剂组成的环氧树脂组合物，并将强化纤维层浸入此环氧树脂组合物中。3.根据权利要求1所述，需要将一次预浸料与含有环氧树脂及溶解于环氧树脂的环氧树脂...
【专利技术属性】
技术研发人员：张银坤，马俊杰，
申请(专利权)人：四川鑫达企业集团有限公司，
类型：发明
国别省市：四川,51