The invention belongs to the technical field of supercapacitors and aims to solve the problems of poor cyclic stability and low rate performance caused by poor conductivity of existing two-dimensional hydrotalcite. The product is made from nickel salt, cobalt salt, urea and PVP, and three-dimensional porous flower-like structure hydrotalcite has been successfully prepared without template. The electrode material was used as working electrode and showed high specific capacitance, excellent rate characteristics and good cyclic stability. At the same time, this method can be used to synthesize other kinds of three-dimensional porous flower-like hydrotalcite.
【技术实现步骤摘要】
一种花状Ni-Co水滑石电极材料的制备
本专利技术属于超级电容器
，具体涉及一种花状Ni-Co水滑石电极材料的制备。
技术介绍
超级电容器作为一种新型的能源存储器件，近年来受到广大科研工作者的关注。由于其功率密度高、循环寿命长、充电速度快、温度范围宽以及绿色安全等优点，在电子工业领域得到了广泛的应用。超级电容器根据储能机理不同，可以分为双电层电容器和赝电容超级电容器两类。与传统的双电层电容器相比，赝电容电容器能够储存更多的电荷，因此具有更高的比电容。赝电容电容器又称法拉第准电容器，其电极材料主要为过渡金属氧化物和导电聚合物两种，其储存电荷的过程不但包括双电层电容器的存储方式，而且包括电解液中离子在电极活性物质中是通过氧化还原反应过程存储的。这种氧化还原反应在电极表面发生的同时也可在整个电极内部发生，赝电容电容器作为双电层电容器的一种补充形式，往往可获得更高的电容量和能量密度。层状双金属氢氧化物，又称水滑石（LDHs），作为一类重要的二维层状材料，由于其层板元素的高分散性、双金属元素的比例可调变性及层间阴离子的可交换性，因此在电化学功能电极领域展现出了巨大的研...
【技术保护点】
1.一种花状Ni‑Co水滑石电极材料的制备，其特征在于一种花状Ni‑Co水滑石电极材料的制备不需要添加任何模板，以镍盐、钴盐、尿素、PVP为原料，水热法合成了三维多孔花状结构。
【技术特征摘要】
1.一种花状Ni-Co水滑石电极材料的制备，其特征在于一种花状Ni-Co水滑石电极材料的制备不需要添加任何模板，以镍盐、钴盐、尿素、PVP为原料，水热法合成了三维多孔花状结构。2.根据权利要求1所述的，其特征在于一种花状Ni-Co水滑石电极材料的制备，所述的双金属元素为镍、钴元素。3.根据权利要求1所述的，其特征在于一种花状Ni-Co水滑石电极材料的制备，所述的合成方法为水热...
【专利技术属性】
技术研发人员：谭立超，张璐璐，马慧媛，宋秀梅，李洪彬，
申请(专利权)人：哈尔滨理工大学，
类型：发明
国别省市：黑龙江,23
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。