The invention discloses a preparation method of a spherical nanometer nickel molybdate electrode material with high recycling performance, belonging to the technical field of material preparation and energy storage. A spherical nano-material consisting of lamellar superposition was prepared by solvothermal method using water and ethylene glycol as solvents and molybdenum and nickel sources with the same molar ratio as reactants at 160 ~C. The thickness of the lamellar was about 20 nm. At the same time, the nanometer material prepared by the invention has excellent electrochemical cycling performance, and the specific capacitance reaches 115% of the initial value after 600 cycles. The preparation of the nano-materials has the advantages of low cost, easy synthesis and no pollution. It has a good practical application prospect.
【技术实现步骤摘要】
一种高循环性能球状纳米钼酸镍电极材料的制备方法
本专利技术属于材料制备及储能
，具体涉及溶剂热与煅烧相结合的方法制备纳米钼酸镍电极材料，该材料具有相对优异的电化学储能性能以及极其优异的循环性能。
技术介绍
超级电容器又名电化学电容器，是20世纪80年代发展起来的一种介于传统电容器与蓄电池之间的一种新型的储能器件。相比于电池，该器件具有优良的充放电性能和比较大的储能性能，其具有功率密度高、循环寿命长、充电速度快、无污染等特点。基于此，超级电容器受到了世界各国研究人员的青睐。目前在超级电容器领域中，MnO2是商用最为成功的材料，但因其比容量相对较低，循环性能相对较差制约了该材料的发展。近年来钴基和镍基材料成为人们关注较多的对象，而镍基材料由于较高的理论比电容而受到人们的广泛关注，相对于单一氧化镍材料来说，二元镍基氧化物由于其比单一氧化物材料有更好的性能，钼镍二元金属氧化物因其资源丰富、环境友好以及具有多重的氧化态和较好导电性能受到了人们越来越多的关注。当前人们已制得了多种形貌的NiMoO4纳米材料，例如申请号为201711169041.3的中国专利合成了一种多层...
【技术保护点】
1.一种高循环性能球状纳米钼酸镍电极材料的制备方法步骤如下：首先称取1.5 mmol的六水合硫酸镍和1.5 mmol的二水合钼酸钠,并将其溶解于盛放18 ml蒸馏水与18 ml乙二醇混合溶剂的小烧杯中，在磁力搅拌器下均匀溶解，后取出磁子，将混合溶液转移到容积为50 ml的含聚四氟乙烯内胆的不锈钢高压反应釜里，密封高压反应釜，放置于160℃的烘箱里，12 小时后将其取出，自然冷却至室温，用8000转每分钟转速，离心5分钟，得到沉淀，用蒸馏水与乙醇交替洗涤各三次，将沉淀放入60℃的烘箱里，放置12小时烘干后将其取出，在500℃的马弗炉里煅烧4小时，得到最终产品。
【技术特征摘要】
1.一种高循环性能球状纳米钼酸镍电极材料的制备方法步骤如下：首先称取1.5mmol的六水合硫酸镍和1.5mmol的二水合钼酸钠,并将其溶解于盛放18ml蒸馏水与18ml乙二醇混合溶剂的小烧杯中，在磁力搅拌器下均匀溶解，后取出磁子，将混合溶液转移到容积为50ml的含聚四氟乙烯内胆的不锈钢高压反应釜里，密封高压反应釜，放置于160℃的烘箱里，12小时后将其取出，自然冷却至室温，用8000转每分钟转速，离心5分钟，得到沉淀，用蒸馏水与乙醇交替洗涤各三次，将沉淀放...
【专利技术属性】
技术研发人员：宋吉明，张国峰，牛和林，毛昌杰，陈京帅，
申请(专利权)人：安徽大学，
类型：发明
国别省市：安徽,34