The invention provides a method for using waste powder as filler of lacquer, the weight of a number of components and components as follows: silicone acrylic emulsion 180 ~ 300, 5 ~ 20 coalescents, waste powder 50 - 200, 400 - 800, sand rock slices 10 - 20, 10 auxiliaries ~ 25, the film-forming assistant or a mixture of several glycol ether, propylene glycol, alcohol ester, a waste powder for the waste granite powder, waste marble powder, the mixture of additives including one or several kinds of defoaming agent, thickening agent, dispersing agent, waterproofing agent, germicide, of the penetrant. The invention of lacquer to waste powder as filler with high performance polymer emulsion, natural sand and various additives prepared can be used in construction engineering, interior decoration, can achieve the natural stone decorative effect.
【技术实现步骤摘要】
一种以废石粉为填料的真石漆
本专利技术属于建筑材料领域，涉及一种以废石粉为填料的真石漆。
技术介绍
随着建筑装修的逐步流行，真石漆越来越受到欢迎，真石漆可以装饰出酷似天然花岗岩、大理石的效果，真石漆的主要是由高性能聚合物乳液、天然石粉以及多种助剂配制而成，其施工方便，可用于水泥墙体、砖墙、石棉板、木板等材料，可在高档住宅、庭院、高楼大厦等领域得到广泛应用。
技术实现思路
本专利技术的目的在于提供一种真石漆，该真石漆以废石粉为填料，配以高性能聚合物乳液、天然彩砂和各种助剂制备而成，可应用于建筑室内外装修工程，可以达到天然石材的装饰效果。本专利技术采用的技术方案为：一种以废石粉为填料的真石漆，其特征在于，组份及各组份的重量份数如下：硅丙乳液180～300份，成膜助剂5～20份，废石粉50～200份，彩砂400～800份，岩片10～20份，助剂10～25份。所述成膜助剂为乙二醇丁醚、丙二醇、醇酯的一种或几种的混合物。所述废石粉为废花岗石粉、废大理石粉的一种。所述废石粉的粒径范围为100～200目。所述彩砂的粒径范围为10～100目。所述助剂包括消泡剂、增稠剂、分散剂、防水剂、杀菌剂、渗透剂的一种或几种的混合物。本专利技术所具有的有益效果：本专利技术真石漆配方设计合理，配方中加入了废石粉，一方面可以高效利用工业废弃物废石粉，提供了一种废石粉的利用途径，另一方面加入了废石粉可以替代部分彩砂，降低成本，并能提供天然石材的各种色彩。具体实施方式为了使本专利技术所解决的技术问题、技术方案及有益效果更加清楚明白，以下结合实施例，对本专利技术作进一步的说明。应当理解，此处所描述的...
【技术保护点】
一种以废石粉为填料的真石漆，其特征在于，组份及各组份的重量份数如下：硅丙乳液 180～300份，成膜助剂 5～20份，废石粉 50～200份，彩砂 400～800份，岩片 10～20份，助剂 10～25份。
【技术特征摘要】
1.一种以废石粉为填料的真石漆，其特征在于，组份及各组份的重量份数如下：硅丙乳液180～300份，成膜助剂5～20份，废石粉50～200份，彩砂400～800份，岩片10～20份，助剂10～25份。2.根据权利要求1所述的以废石粉为填料的真石漆，其特征在于，所述成膜助剂为乙二醇丁醚、丙二醇、醇酯的一种或几种的混合物。3.根据权利要求1所述的以废石粉为填料的真石漆，其特征在于，...