The patent belongs to the field of catalyst preparation, in particular to a preparation method of vanadium oxide catalyst for oxidative dehydrogenation of propane to propylene. The vanadium oxide catalyst is supported by mesoporous graphite phase carbon nitride. The preparation method of the catalyst is that the mesoporous graphite phase carbon nitride is impregnated with methanol solution containing vanadium, and the vanadium oxide catalyst supported on the mesoporous graphite phase carbon nitride is prepared by drying, solvent removal and heat treatment. The catalyst was applied to the oxidative dehydrogenation of propane with the ratio of C3H8/O2/N2=1/1/4 (total flow rate: 12-30 mL.min).
【技术实现步骤摘要】
一种用于丙烷氧化脱氢的氧化钒催化剂及其制备方法
本专利涉及一种负载的氧化钒催化剂的制备方法及其催化丙烷氧化脱氢制备丙烯的应用。
技术介绍
丙烯是一种重要的有机化工原料，广泛应用于丙烯腈、塑料和橡胶等合成，也是仅次于乙烯的全球需求量第二的化工单体。丙烯主要来源于石脑油蒸气裂解和石油的催化裂化。随着经济的发展和资源的短缺，以石油为原料的传统合成工艺已远远满足不了市场对丙烯日益增长的需求。我国有着丰富的天然气资源，其中含有6％左右(体积分数)的丙烷，同时丙烷在液化石油气中也约占60％。因此将价格低廉，来源丰富的丙烷定向转化为高附加值的丙烯已成为了当今多相催化领域极具挑战的前沿课题之一。丙烷直接脱氢制备丙烯(CH3–CH2–CH3+O2→CH3–CH＝CH2+H2O)存在着热力学受限、操作温度高(600–700℃)、催化剂容易积碳失活的缺点。相比之下，丙烷氧化脱氢工艺不受热力学平衡限制，反应温度(500–550℃)较丙烷直接脱氢体系低，且无积碳，催化剂无需频繁再生。因此丙烷氧化脱氢制备丙烯成为了目前综合利用天然气和炼厂气的一个极有前途的研究方向。然后，丙烷氧化脱氢是一个较...
【技术保护点】
1.一种用于丙烷氧化脱氢的氧化钒催化剂，其特征在于该催化剂使用介孔石墨相氮化碳材料作为催化剂载体，以氧化钒作为催化剂的活性组分。
【技术特征摘要】
1.一种用于丙烷氧化脱氢的氧化钒催化剂，其特征在于该催化剂使用介孔石墨相氮化碳材料作为催化剂载体，以氧化钒作为催化剂的活性组分。2.一种如权利要求1所述的用于丙烷氧化脱氢的氧化钒催化剂，其特征在于所述的介孔石墨相氮化碳的CN元素比为0.7–5.0，孔径在5–15nm，比表面为100–500m2·g-1，具有石墨晶相结构。3.如权利要求1所述的一种用于丙烷氧化脱氢的氧化钒催化剂的制备方法，其特征在于该方法是按照以下步骤进行的：(1)将含钒的无机或有机盐的活性组分，如偏钒酸铵或乙酰丙酮氧钒溶解在水或甲醇溶液中...
【专利技术属性】
技术研发人员：许杰，干玉林，马丁阳，洪颖，薛冰，李永昕，
申请(专利权)人：常州大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。