The invention relates to a self-compacting concrete, which comprises the following components expressed in weight fractions: 410 420 portions of cement; 50 60 portions of fly ash; 30 35 portions of slag powder; 750 760 portions of sand; 970 980 portions of coarse aggregate; 10 15 portions of admixtures; 28 35 portions of expansive agent; 150 160 portions of water; coarse aggregate including stone with a weight ratio of 5:1. The additive consists of polycarboxylate superplasticizer and binder with a mass ratio of 2:1. Expansion agent and composite phase change material are added into concrete to fill the internal voids of self-compacting concrete and reduce the internal cracks of concrete.
【技术实现步骤摘要】
自密实混凝土及其制备方法
本专利技术涉及一种自密实混凝土及其制备方法。
技术介绍
自密实混凝土拌和物具有足够的塑性粘度，浇筑时在自重下能够流动、填充密实，在致密钢筋中也能够完全填充模板，获得很好的均质性。授权公告号为CN101805160B的专利公开了一种自密实混凝土，在混凝土中浆料混合物包括水泥、粉煤灰，其中粉煤灰包括粉煤灰漂珠和碱性活化粉煤灰漂珠，粉煤灰漂珠和碱性活化粉煤灰漂珠具有耐温隔热的特点，在施工过程中水泥的水化反应产生大量的热，热量聚集在混凝土内部不易散发，而表面的热量散发较快，导致混凝土内部和表面之间形成较大的温差，导致内外温差不一致，当受到较大外力时，混凝土内部或者表面可能产生裂缝，影响自密实混凝土的强度。
技术实现思路
本专利技术的目的在于提供一种自密实混凝土及其制备方法，在混凝土中加入膨胀剂和复合相变材料，填充满自密实混凝土内部空隙，减少混泥土内部裂缝。本专利技术的上述目的是通过以下技术方案得以实现的：一种自密实混凝土，包括以下以重量份数表示的组分：水泥410-420份；粉煤灰50-60份；矿渣粉30-35份；砂750-760份；粗骨料970-98...
【技术保护点】
1.一种自密实混凝土，其特征在于，包括以下以重量份数表示的组分：水泥410‑420份；粉煤灰50‑60份；矿渣粉30‑35份；砂750‑760份；粗骨料970‑980份；外加剂10‑15份；膨胀剂28‑35份；水150‑160份；其中粗骨料包括重量比为5:1的石子和相变陶粒，外加剂包括质量比为2:1的聚羧酸减水剂和粘结剂。
【技术特征摘要】
1.一种自密实混凝土，其特征在于，包括以下以重量份数表示的组分：水泥410-420份；粉煤灰50-60份；矿渣粉30-35份；砂750-760份；粗骨料970-980份；外加剂10-15份；膨胀剂28-35份；水150-160份；其中粗骨料包括重量比为5:1的石子和相变陶粒，外加剂包括质量比为2:1的聚羧酸减水剂和粘结剂。2.根据权利要求1所述的自密实混凝土，其特征在于，相变陶粒包括质量比为1:（2-2.5）的高强陶粒和石蜡。3.根据权利要求2所述的自密实混凝土，其特征在于，粘结剂为环氧改性丙烯酸酯共聚乳液。4.根据权利要求2所述的自密实混凝土，其特征在于，水泥为P.O.42.5级混凝土，28天强度≥58.2MPa。5.根据权利要求2所述的自密实混凝土，其特征在于，粉煤灰为F类Ⅰ级，需水量比≤92%，细度≤6%，烧失量≤1.5%。6.根据权利要求2所述的自密实混凝土，其特征在于，砂为Ⅱ区中砂，细度模数为2.7-2.9。7.根据权利要求2...
【专利技术属性】
技术研发人员：曹有来，郑红高，张爱萍，施勇，
申请(专利权)人：北京中实上庄混凝土有限责任公司，
类型：发明
国别省市：北京,11