The present invention discloses a lithium-sulfur battery, which breaks the Convention and does not install all sulfur on the positive electrode, leaving only a small part as the seed on the positive electrode to guide sulfur to precipitate on the positive electrode, and the negative electrode does not use lithium, but uses conventional graphite or silicon and other materials. Lithium and sulfur are dissolved in the electrolyte solvent in the form of salt. The lithium-sulfur battery manufactured by the invention can avoid the problem of positive electrode dissolution after discharge of conventional lithium-sulfur battery, and has high energy density and long cycle life.
【技术实现步骤摘要】
一种锂硫电池
本专利技术属于锂离子电池领域，具体涉及一种锂硫电池。
技术介绍
锂硫电池是近年来大家研究比较火热的一种锂离子电池，其采用硫元素单质正极材料，锂元素单质为负极材料，由于硫的理论克容量高达1672mAh/g，锂的理论克容量高达3850mAh/g，因而锂硫电池理论能量密度高达2600Wh/kg，是常规锂离子电池能量密度的10~20倍，并且硫在自然界中储量丰富，价格便宜，还有硫是一种对环境友好的元素，对环境基本没有污染，是一种非常有前景的锂电池。但是锂硫电池目前技术尚未成熟，不能大批量生产的主要原因是锂硫电池放电后形成的硫化锂会溶解在电解液中，向负极迁移造成活性物质的损失；另外，锂离子进入硫晶格以及从硫晶格中脱嵌会导致硫的体积较大的变化，从而造成硫的坍陷和脱落；还有，硫作为非金属元素，导电性非常差，在室温条件下，其电导率只有5.0×10-30S·cm-1，电池放电形成的产物产物Li2S2和Li2S也是电子绝缘体，不利于电池的高倍率性能。
技术实现思路
针对以上问题，本专利技术采取了很多改进措施，逆其道而行之，既然硫化锂容易溶解到电解液中，那就将硫和锂以硫化锂的形...
【技术保护点】
1.一种锂硫电池，其特征在于，该电池由正极、负极和电解液组成，所述的正极不将全部的硫装在正极中，仅留一小部分硫在正极中作为种子，用来引导硫在正极的析出，所述负极采用石墨或者硅材料，所述的电解液溶解有锂和硫的盐。
【技术特征摘要】
1.一种锂硫电池，其特征在于，该电池由正极、负极和电解液组成，所述的正极不将全部的硫装在正极中，仅留一小部分硫在正极中作为种子，用来引导硫在正极的析出，所述负极采用石墨或者硅材料，所述的电解液溶解有锂和硫的盐。2.根据权利要求1所述的一种锂硫电池，其特征在于，所述正极是将少量硫、石墨烯、碳纳米管、发孔剂和粘结剂混合成浆状，然后涂布在集流体上烘干后制成的。3.根据权利要求1所述的一种锂硫电池，其特征在于，所述负极是将石墨或硅材料和导电剂、粘结剂混合成浆状，然后涂布...
【专利技术属性】
技术研发人员：李义，李国敏，
申请(专利权)人：深圳格林德能源有限公司，
类型：发明
国别省市：广东,44