The invention relates to a synthesis method of ZSM_12 molecular sieve. First, aluminum source is added to water in proportion, then silicon source and template isopropylamine are added successively, stirred evenly at room temperature, the mixed solution is transferred to a high-pressure reactor, and the mixed solution is hydrothermally crystallized at 160 C for 70 hours. After cooling, the product is washed and dried. ZSM_12 molecular sieves synthesized by this method can be used in methane aromatization, methanol conversion, alkane dehydrogenation to olefins, olefin disproportionation, xylene isomerization, toluene alkylation and other acid catalytic reactions.
【技术实现步骤摘要】
一种合成ZSM-12分子筛的方法
本专利技术属于无机多孔材料制备
，涉及一种合成ZSM-12分子筛的方法。
技术介绍
1971年美国Mobil公司公开了高硅ZSM-12分子筛的合成方法，其属于丝光沸石类，结构类型为MTW。ZSM-12分子筛属于单斜晶系（C2/m），晶胞参数为a=2.488nm，b=0.502nm，c=1.215nm，β=107.7°[1]，每个晶胞含28个T原子。ZSM-12分子筛骨架结构具有一维线性非交叉孔道，孔道尺寸为0.57×0.61nm，可用于裂化、加氢裂化、异构化和芳烃烷基化等多种反应中的催化剂，尤其对正碳离子反应具有良好的催化活性和选择性。模板剂类型显著影响ZSM-12分子筛的形貌、酸性和纹理特征，进而调变其催化性能。目前，合成ZSM-12分子筛的模板剂有以下五类：（1）四乙基铵根离子做模板剂。公开号为US3832449（A）（公开日1974年8月27日）的专利和公开号为US4112056（A）（公开日1978年9月5日）的专利公开一种以四乙基铵根为模板剂合成ZSM-12分子筛的方法。合成溶胶物质的量的配比为：SiO2/Al2O...
【技术保护点】
1.一种合成ZSM‑12分子筛的方法，其特征在于：按比例先将铝源加入水中，再依次加入硅源和模板剂异丙胺，在室温下搅拌均匀，将混合溶液转入高压反应釜，在160℃下水热晶化70小时，冷却后洗涤、干燥，即得产品。
【技术特征摘要】
1.一种合成ZSM-12分子筛的方法，其特征在于：按比例先将铝源加入水中，再依次加入硅源和模板剂异丙胺，在室温下搅拌均匀，将混合溶液转入高压反应釜，在160℃下水热晶化70小时，冷却后洗涤、干燥，即得产品。2.根据权利要求1所述的方法，其特征在于：所述的铝源为偏铝酸钠。3.根据权利要求1或2所述的方法，其特征在于：所述的硅源为M-5。...
【专利技术属性】
技术研发人员：张海荣，潘启亮，强丁丁，刘红艳，冯逸伟，沈腊珍，王蕊，宋卫红，邵云雪，蒋煜，郭永，
申请(专利权)人：山西大同大学，
类型：发明
国别省市：山西,14
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。