The invention relates to synthesis of semi rigid multidentate ligand cobalt compounds, is prepared by hydrothermal synthesis, 4,4 ', 4 \(1,3,5 three phenoxy) autoclave of three benzoic acid 0.05mmol, six hydrated cobalt nitrate 0.25mmol and distilled water 10 20mL into the Teflon liner. Ultrasound after dissolving into 120 DEG C oven reaction 3 5 days, and then naturally cooled to room temperature, to obtain the target compound semi rigid multidentate ligand cobalt compounds; crystal suitable reagent for washing, and dry naturally, the yield was 72.5% (calculated by the element Co); element analysis value: C 54.04%, H 3.12%, O 27.95%, Co 14.80%; theoretical value: C 54.14% H 3.01%,, O 28.08%, Co 14.77%.
【技术实现步骤摘要】
半刚性多齿配体钴化合物的合成
本专利技术涉及半刚性多齿配体钴化合物的合成，属于合成化学领域。
技术介绍
金属-有机骨架材料(Metal-Organicframeworks,简写MOFs)，又或称之为配位聚合物(Coordinationpolymers，简写CPs)，是指有机配体和金属离子以配位键的形式连接而成的一类具有丰富的孔道结构、庞大的比表面积的周期性无限网络结构的晶体材料。关于金属-有机骨架材料的研究同时跨越了有机化学、无机化学、配位化学、材料化学、物理化学、超分子化学、晶体工程学以及拓扑学等多个学科领域，同时，因其丰富多样的结构导致的其具有多种物理化学性质，如：其在催化、气体吸附与分离、光学、磁学和离子交换等方面都有应用，这是其他材料所无法比拟的。这也使得世界上的研究者们对金属-有机骨架材料产生了极大的研究兴趣。到目前为止，已有上千余种金属-有机骨架材料被成功合成并报道出来。
技术实现思路
本专利技术所要解决的技术问题是提供半刚性多齿配体钴化合物的合成，技术方案如下：是用水热合成法合成的，取4,4′，4″-(1,3,5-三苯氧基苯)三苯甲酸0.05mmol、六水合硝酸钴0.25mmol以及蒸馏水10-20mL放入聚四氟乙烯作内衬的高压反应釜中，超声溶解后，放入120℃烘箱内反应3-5天，然后自然冷却到室温，即得到目标化合物半刚性多齿配体钴化合物；用合适的试剂洗涤晶体，并自然晾干，产率为72.5％(以元素Co计算)；元素分析值：C54.04％，H3.12％，O27.95％，Co14.80％；理论值：C54.14％，H3.01％，O28.08％，Co14....
【技术保护点】
半刚性多齿配体钴化合物的合成，其特征在于，包括：是用水热合成法合成的，取4,4′，4″‑(1,3,5‑三苯氧基苯)三苯甲酸0.05mmol、六水合硝酸钴0.25mmol以及蒸馏水10‑20mL放入聚四氟乙烯作内衬的高压反应釜中，超声溶解后，放入120℃烘箱内反应3‑5天，然后自然冷却到室温，即得到目标化合物半刚性多齿配体钴化合物；用合适的试剂洗涤晶体，并自然晾干，产率为72.5％(以元素Co计算)；元素分析值：C54.04％，H 3.12％，O 27.95％，Co 14.80％；理论值：C 54.14％，H 3.01％，O 28.08％，Co 14.77％。
【技术特征摘要】
1.半刚性多齿配体钴化合物的合成，其特征在于，包括：是用水热合成法合成的，取4,4′，4″-(1,3,5-三苯氧基苯)三苯甲酸0.05mmol、六水合硝酸钴0.25mmol以及蒸馏水10-20mL放入聚四氟乙烯作内衬的高压反应釜中，超声溶解后，放入120℃烘箱内反应3-5天，然后自然冷却到室温，即得到目标化合物...