一种热固成型工艺排气的方法技术
A method of exhausting in thermosetting process
The invention belongs to the technical field of thermosetting material processing, in particular to a method for exhausting the thermosetting molding process. It includes the following effective steps: A, first set the exhaust hole on the die wall, and at least the exhaust hole runs through the end of the die wall; B, and then the inner surface of the mold is set up a number of uniform distribution and the width of the deep gap between 0.2mm and 0.3mm; C, and finally the deep gap is connected with the exhaust hole. By providing a method of exhausting in a thermosetting process, a deep gap in the inner surface of the mold is set by the exhaust hole set on the wall of the mold. When high temperature and high pressure, the deep gap and the exhaust hole form the unique passage of the exhaust and no leakage, so as to achieve the barrier free discharge of the steam at high temperature and high pressure. At the same time, the method provided by the invention reduces the exhaust process, thus shortens the processing time and improves the production efficiency. One
【技术实现步骤摘要】
一种热固成型工艺排气的方法
本专利技术属于热固性材料加工
，尤其涉及一种热固成型工艺排气的方法。
技术介绍
热固性材料以热固性树脂为主要成分，配合以各种必要的添加剂通过交联固化过程成形成制品的材料。在制造或成型过程的前期为粉状或颗粒状加入热固性胶黏剂，热固化后成型。常见的热固性胶水有酚醛胶，脲醛胶，异氰酸酯以及无机胶等。热固成型工艺都会加入胶水，而胶水在加热固化的过程都会产生水蒸气，因为模具是高压闭合的，蒸汽就会被模具锁住无法释放，只有打开模具时，蒸汽才会被释放出来，但排气过早、过迟都不行，过早达不到排气的目的；过迟则因物料表面已固化气体排不出，进而影响产品的性能。因此，这也就使得热固性材料次品率较高，因此，迫切需要一种方法来实现准确及时的排气。
技术实现思路
本专利技术针对上述的热固材料成型工艺所存在的排气不好掌握的技术问题，提出一种设计合理、方法简单、操作方便且能够实现自动排气的热固成型工艺排气的方法。为了达到上述目的，本专利技术采用的技术方案为提供一种热固成型工艺排气的方法，包括以下有效步骤：a、首先在模具的模具壁上设置排气孔，排气孔至少贯穿模具壁的一端；...
【技术保护点】
1.一种热固成型工艺排气的方法，其特征在于，包括以下有效步骤：
【技术特征摘要】
1.一种热固成型工艺排气的方法，其特征在于，包括以下有效步骤：a、首先在模具的模具壁上设置排气孔，排气孔至少贯穿模具壁的一端；b、然后在模具的内表面设置若干个均匀分布且宽度在0.2mm～0.3mm之间的深层缝隙；c、最后是深层缝隙与排气孔连通即可。2.根据权利要求1所述的热固成型工艺排气的方法，其...
【专利技术属性】
技术研发人员：董作彬，
申请(专利权)人：青岛一宇集团有限公司，
类型：发明
国别省市：山东,37