The invention provides a lake bitumen compound bitumen modified bitumen, consisting of a component of the following weight parts: 50~80 bitumen, 10~25 biologic bitumen and 10~25 parts of Lake bitumen. The invention also provides a preparation method of the lake asphalt compound biological asphalt modified asphalt. The invention uses the lake bitumen and the biological bitumen as modifier to modify the matrix bitumen. The incorporation of the bio asphalt improves the fatigue resistance and low temperature cracking performance of the matrix petroleum asphalt. The addition of the lake bitumen improves the high temperature performance of the bitumen, thus comprehensively and comprehensively improving the high temperature and low temperature of the matrix bitumen. Durability. The performance of modified asphalt is outstanding and has good technical and economic prospects. The preparation method of the lake asphalt compound biological asphalt modified asphalt is simple and easy to popularize.
【技术实现步骤摘要】
一种湖沥青复配生物沥青改性沥青及其制备方法
本专利技术涉及改性沥青
，具体涉及一种湖沥青复配生物沥青改性沥青及其制备方法。
技术介绍
随着我国公路建设的迅猛发展，沥青路面以其优越性能在全国范围内得到了广泛应用，沥青的消费量在近年来大幅增长。目前路用沥青大部分是原油中提炼的石油沥青，然而石油是不可再生的稀缺性资源，由于过度开采和使用，石油资源日渐枯竭。因此，亟需寻找一种具有优良路用性能的可再生材料，以减轻沥青生产和利用过程中对石油资源的依赖。生物沥青是一种生物质材料经过一定的物理化学工艺处理制得具有胶结料性能的类似于石油沥青的材料。具有可再生、清洁、经济环保等性能，在满足规范要求的情况下，将生物沥青作为改性剂加入基质石油沥青当中，可以大大减少石油沥青的用量，这对节约资源和环境保护意义重大。然而，生物沥青软化点低、黏度小，在高温稳定性方面存在技术缺陷。湖沥青是石油不断从地壳中冒出，存在于天然湖中，经长期沉淀、变化、硬化产生的沥青类物质。由于与自然环境长期共存，所以湖沥青高温性能非常稳定，将其作为改性剂掺入沥青中，可改善沥青的高温性能。
技术实现思路
本专利技术的目的...
【技术保护点】
一种湖沥青复配生物沥青改性沥青，其特征在于由如下重量份的组分组成：基质沥青50～80份，生物沥青10～25份，湖沥青10～25份。
【技术特征摘要】
1.一种湖沥青复配生物沥青改性沥青，其特征在于由如下重量份的组分组成：基质沥青50～80份，生物沥青10～25份，湖沥青10～25份。2.根据权利要求1所述湖沥青复配生物沥青改性沥青，其特征在于：所述湖沥青为特立尼达湖沥青。3.根据权利要求1所述湖沥青复配生物沥青改性沥青，其特征在于：所述生物沥青为大豆油生物沥青。4.权利要求1至3所述湖沥青复配生物沥青改性沥青的制备方法，其特征在于包括如下步骤：（1）将块状湖沥青加入粉碎机中粉碎后过筛，制得湖沥青改性剂；（2）将生物沥青水浴加热并以3500～5000r/min的速度剪切30～60min，制得生物沥青改性剂；（3）将湖沥青改...
【专利技术属性】
技术研发人员：赵宇，程小亮，王阳，王瑞金，
申请(专利权)人：中冶南方城市建设工程技术有限公司，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。