Modified road bitumen

The present invention discloses a modified road asphalt, which is prepared from the raw material of the following weight: 95 bitumen 105, styrene butadiene rubber 5, 8 copies of chloroprene rubber, 8 polyvinyl chloride 1, 0.5 polyvinyl chloride, 5 N, 0.5 benzoic acid, 0.5 benzoic acid and methyl benzaldehyde. The flame retardant is 1, 5, and 0.2, 0.9. The modified road bitumen of the present invention increases the softening point of asphalt, decreases the penetration of the needle, increases the stability of the high temperature, increases the low temperature ductility greatly, and increases the crack resistance of the low temperature remarkably.

【技术实现步骤摘要】
改性道路沥青
本专利技术涉及沥青改性
，具体涉及一种改性道路沥青。
技术介绍
随着我国公路建设的飞速发展，公路通车里程逐年快速增长的同时，公路的车流量与重载车辆迅速增加，路面磨耗较以前大大加剧，提高路面质量，延长公路的使用寿命，变得刻不容缓。特别是在夏天或者是在一些容易出现高温、多雨天气的区域，公路路面粘度就会极大的降低，加之车流的通过，公路就很容易被损坏。沥青是常用于制备铺路和屋顶材料的材料。在道路建造和道路铺设工业中，成熟实用的方法是利用热的流体沥青涂覆骨料材料，例如沙子、砂砾、碎石或其混合物，在其还热的时候将涂覆的材料在路基或先前建造的道路上铺展为均匀层，并通过重型压路机滚压来将均匀层压实，以形成表面光滑的道路。沥青与骨料材料例如沙子、砂砾、碎石或其混合物的组合被称作“沥青混凝土”。沥青，也被称作“沥青混凝土粘合剂”，通常是一种含有沥青质、树脂和油类的液体粘合剂。它可以是天然存在的，也可以是从原油的残留物中获得的，或在原油精炼过程后获得的。沥青通常包含具有高沥青质含量的烃类。沥青也可以经过一些进一步的处理，从而使沥青组份经过氧(如空气)或化学组份(如磷酸)的氧化。随着我国本文档来自技高网...

【技术保护点】
一种改性道路沥青，其特征在于，由下述重量份的原料制备而成：沥青95‑105份、丁苯橡胶5‑15份、氯丁橡胶2‑8份、聚氯乙烯1‑5份、N‑异丙基‑N‑苯基‑对苯二胺0.5‑5份、邻苯二甲酸二甲酯1‑10份、对甲基苯甲醛0.1‑1份、阻燃剂1‑5份、分散剂0.2‑0.9份。

【技术特征摘要】
1.一种改性道路沥青，其特征在于，由下述重量份的原料制备而成：沥青95-105份、丁苯橡胶5-15份、氯丁橡胶2-8份、聚氯乙烯1-5份、N-异丙基-N-苯基-对苯二胺0.5-5份、邻苯二甲酸二甲酯1-10份、对甲基苯甲醛0.1-1份、阻燃剂1-5份、分散剂0.2-0.9份。2.如权利要求1所述的改性道路沥青，其特征在于：所述的阻燃剂为二乙基磷酸铝、甲基丙酸基次膦酸铝、2-羧乙基苯基次膦酸铝中一种或多种的混合物。3.如权利要求2所述的改性道路沥青，其特征在于：所述的阻燃剂由...