冷补沥青液及其制备方法技术
Cold filled asphalt liquid and its preparation method
The invention discloses a cold patching asphalt solution, which relates to the technical field of highway engineering. The cold fill asphalt is made up of matrix petroleum bitumen, diluent, styrene butadiene styrene block copolymer and additive. The preparation method of cold fill bitumen liquid by weighing raw material and stirring, then cutting the middle product, then making the modified asphalt, then preparing the additive, will make the additive. The bitumen solution is prepared by shearing the additives, modified asphalt and diluent in the container. The invention provides a cold - filled asphalt liquid and its preparation method, which reduces the production cost of the cold - filled asphalt liquid. The cold - filled asphalt liquid has good adhesion, and the prepared cold - filled asphalt mixture has good construction and ease of construction and water stability.
【技术实现步骤摘要】
冷补沥青液及其制备方法
本专利技术属于公路工程
，涉及一种冷补沥青液及其制备方法。
技术介绍
在我国，高等级公路使用范围比较广，一般采用的都是沥青路面的结构形式。沥青路面与水泥路面相比，具有施工时间短、噪音小、行驶舒适、修补方便等特点。但是沥青路面在行车荷载和自然环境共同作用下，容易发生车辙、裂缝、剥落等一些病害。如何对这些病害路面进行快速维修并且尽早开放交通是十分重要的。冷拌冷铺技术是中国道路修补技术的一个巨大的进步，但是同欧美国家相比，中国起步比较晚，对冷补沥青混合料产品的了解源自于进口产品，其研究是在引进国外产品之后才开始的。由于国外产品比较昂贵，一些高校和企业合作开始对冷补沥青混合料进行研究和开发。高校的一些专家开始开发冷补沥青混合料并把它运用到工程中去，不论是在研究还是应用都积累了大量的宝贵经验，我国沥青路面病害修补技术飞速发展，经济效益和环境效益非常显著。但是至今我国冷补沥青混合料的性能仍然有许多的不足，一些关键性技术没有得到解决，施工和易性和初始强度还存在问题，所以这就需要不断努力来进一步完善冷补沥青混合料。冷补沥青混合料性能主要取决于冷补沥青...
【技术保护点】
冷补沥青液，其特征在于，按照质量份数，由基质石油沥青100份、稀释剂20～35份、苯乙烯‑丁二烯‑苯乙烯嵌段共聚物2～4份、添加剂7～15份组成。
【技术特征摘要】
1.冷补沥青液，其特征在于，按照质量份数，由基质石油沥青100份、稀释剂20～35份、苯乙烯-丁二烯-苯乙烯嵌段共聚物2～4份、添加剂7～15份组成。2.根据权利要求1所述的冷补沥青液，其特征在于，所述稀释剂为0#柴油。3.根据权利要求1所述的冷补沥青液，其特征在于，所述添加剂由2～4.5份的C5C9共聚树脂、2～4.5份的乙烯-醋酸乙烯共聚物、2～4.5份的溶剂、0.5～0.8份的抗剥落剂组成。4.根据权利要求3所述的冷补沥青液，其特征在于，所述溶剂为油酸。5.根据权利要求3所述的冷补沥青液，其特征在于，所述抗剥落剂为PM-JL-06A型沥青抗剥落剂。6.一种如权利要求1-5任何一项所述的冷补沥青液的制备方法，其特征在于，按照以下步骤进行：步骤1、将称量好的基质石油沥青、苯乙烯-丁二烯-苯乙烯嵌段共聚物依次加入到反应容器中，温度150±5℃，加热并不断用铁棒搅拌0.5h；步...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。