一种医用耐高温亲水包覆无纺布的制备方法技术
Preparation method of medical high temperature resistant hydrophilic coated non-woven fabric
The invention provides a preparation method of high temperature resistant and hydrophilic nonwoven fabric. By mixing ordinary spunbonded raw materials and high temperature hydrophilic particles in a certain proportion and transferring to the screw extruding and melting to get the melt, the hot melt melt is spun into fiber, and the three layer fiber mesh and the SMS non woven fabric are pressed by the hot rolling mill to form nonwovens. Cloth. The preparation method of the medical high temperature resistant hydrophilic coated non-woven fabric has the advantages of hydrophilicity and non transfer, and can perfectly meet the requirements of high temperature steam sterilization for medical devices.
【技术实现步骤摘要】
一种医用耐高温亲水包覆无纺布的制备方法
本专利技术涉及无纺布制造
，特别涉及一种医用耐高温亲水包覆无纺布的制备方法。
技术介绍
现阶段医疗器械杀菌消毒所采用的方式为高温蒸汽灭菌，包覆材料必须能耐受121℃-135℃的高温，空气的排出，水蒸气的穿透以及包装材料和内含物品的干燥。目前常用的包覆材料有棉布、硬质容器、医用皱纹纸和无纺布。棉布在上世纪80年代以前一直作为最常用的医用包装材料，然而棉布易吸水，棉线排列规则且之间孔径较大，棉布的微生物屏障效能较差。随着反复使用，棉线孔隙会更加扩大，造成微生物屏障性能的进一步下降；棉纤维破裂产生的棉尘也是医源性感染的重要原因。国外许多文献因此不推荐使用棉布单独作为包装材料，而仅作为外包装材料或者额外附加的防尘罩。硬质容器通常由铝合金、不锈钢或者塑料制成，并带有可拆卸可密封的容器盖。通过容器盖上的过滤器，硬质容器可实现灭菌因子的穿透和微生物的屏障。硬制容器也存在着下面的一些局限性，第一，容器较重，不当搬运可能带来人体工学上的伤害。第二，需要延长干燥时间以避免“湿包”现象。第三，锁扣系统和过滤器在使用前需要检查。而且，初次购置...
【技术保护点】
一种医用耐高温亲水包覆无纺布的制备方法，其特征在于该方法包括如下步骤：(1)将普通纺粘原料(H39S‑2或者其他任意纺粘原料均可)与耐高温亲水母粒CPPW036按照一定比例混合；(2)将所述混合搅拌好的原料通过喂料系统(真空抽吸)到大螺杆进行挤压熔融，获得热熔体；(3)将所述热熔体在一定温度、一定压力下进行过滤、计量和分配后进行纺丝，并将纺出的丝经侧冷风冷却，获得初生长丝；(4)将所述初生长丝经过气流分丝的方式，通过狭缝式牵伸器的喇叭口，将初生长丝进行气流牵伸，同时经过牵伸的初生长丝分子链排列整齐，产生强力，形成纤维；(5)将纤维分丝铺网，形成纤网与SMS无纺布基布通过热轧...
【技术特征摘要】
1.一种医用耐高温亲水包覆无纺布的制备方法，其特征在于该方法包括如下步骤：(1)将普通纺粘原料(H39S-2或者其他任意纺粘原料均可)与耐高温亲水母粒CPPW036按照一定比例混合；(2)将所述混合搅拌好的原料通过喂料系统(真空抽吸)到大螺杆进行挤压熔融，获得热熔体；(3)将所述热熔体在一定温度、一定压力下进行过滤、计量和分配后进行纺丝，并将纺出的丝经侧冷风冷却，获得初生长丝；(4)将所述初生长丝经过气流分丝的方式，通过狭缝式牵伸器的喇叭口，将初生长丝进行气流牵伸，同时经...