An aluminum cobalt cobalt boron intermediate alloy and its preparation method. The intermediate alloy consists of the following mass percentages: Al 91.1 ~ 99.1%, Co 0.5 ~ 4.5%, B 0.1 ~ 3%, Fe < 0.15%, Si < 0.10%, and the remaining impurity elements less than 0.15%. Due to the use of aluminum cobalt boron three element intermediate alloy as an iron rich phase change agent, it can not only completely eliminate the existence of needle like iron rich phase and primary iron rich phase, obtain uniform Chinese character like iron rich phase, but also greatly reduce the total amount of intermediate alloy needed to add cobalt and boron elements in step by step, and reduce the process at the same time. It is more suitable for the control of the alloy composition and is more suitable for industrial production. As the lower content of cobalt can cause the precipitation of the primary silicon, the invention is more suitable for the transformation of the iron rich phase of the aluminum alloy with low silicon or low silicon content.
【技术实现步骤摘要】
一种铝-钴-硼中间合金及其制备方法
本专利技术涉及一种铝及铝合金材料中富铁相的变质剂，具体是涉及一种铝-钴-硼中间合金及其制备方法。
技术介绍
铁是铝合金中最为常见的杂质元素，由于铁元素在室温下铝固体中的最大溶解度为0.05wt.%，仅为铝熔体中最大溶解度的1/100～1/34。因此，铁在铝合金中基本都以脆且硬的富铁相形式存在。根据富铁相的晶体结构可分为α-Fe相和β-Fe相，其中β-Fe相为单斜结构，形态呈狭长的针片状，受力时割裂铝基体，并成为裂纹源且沿着富铁相长度方向扩展，极大损害铝合金的塑性。而α-Fe相为体心立方结构，基本形态呈汉字状，对基体的割裂大幅降低，塑性大幅改善。因此，改善富铁相形态是减缓铁元素危害最为常用的方法。目前，改善富铁相形态的方法可总结成两类，第一类是改变富铁相晶体结构来改善富铁相的生长方向，如Mn、Co、Cr、Be、Sc等。第二类是改变富铁相生长速度，如B、RE、Sr、Ca、熔体处理、铸造工艺，采用两类方法相结合不仅可实现β-Fe相向α-Fe的转变，还能细化α-Fe尺寸，改善效果最佳，其中采用两类元素复合添加的方法不仅操作简单，且合金成...
【技术保护点】
一种铝‑钴‑硼中间合金，其特征在于该中间合金由以下质量百分比的成分组成：Al 91.1～99.1%，Co 0.5～4.5%，B 0.1～3.0%，Fe≤0.15%，Si≤0.10%，其余杂质元素≤0.15%。
【技术特征摘要】
1.一种铝-钴-硼中间合金，其特征在于该中间合金由以下质量百分比的成分组成：Al91.1～99.1%，Co0.5～4.5%，B0.1～3.0%，Fe≤0.15%，Si≤0.10%，其余杂质元素≤0.15%。2.根据权利要求1所述的铝-钴-硼中间合金，其特征在于该中间合金采用Co质量分数为1～5%的Al-Co中间合金、B质量分数为3～10%的Al-B中间合金以及纯度为99.5%的工业纯铝作为原材料。3.一种铝-钴-硼中间合金的...
【专利技术属性】
技术研发人员：宋东福，郑开宏，周楠，秦芳诚，杨莉，康跃华，
申请(专利权)人：广东省材料与加工研究所，
类型：发明
国别省市：广东,44