The invention discloses a crack resistant adhesive mortar, which aims to solve the problem of easy cracking of ordinary bonding mortar due to the lowering of external temperature. The technical scheme of the invention is: a anti cracking adhesive mortar, which is made up of dry material and admixture; the dry material is composed of cement, fly ash and fine sand, and the proportion of cement 25~30%, fly ash 15~20% and fine sand 40~50% are respectively, and the admixtures are composed of dispersible latex powder, polypropane and acrylate, and the proportion is respectively, but Dispersive latex powder 0.15~0.20%, polypropylene 0.05~0.10%, acrylate 0.05~0.1%. The invention has the advantages of good adhesive property and excellent crack resistance.
【技术实现步骤摘要】
一种抗裂粘接砂浆
本专利技术属于建筑材料领域,特别涉及一种抗裂粘接砂浆。
技术介绍
粘结砂浆是由水泥、石英砂、聚合物胶结料配以多种添加剂经机械混合均匀而成的一种砂浆。主要用于粘结保温板的粘结剂,也被称为聚合物保温板粘结砂浆。该粘结砂浆采用优质改性特制水泥及多种高分子材料、填料经独特工艺复合而成。保水性好,粘接强度高,耐水、耐老化效果好,同时具有良好的抗冲击性。已在建筑外墙以及保温板粘接领域占有很大市场份额。但粘接砂浆在冬季施工时受温度影响很容易发生开裂,施工完成后也会因发生墙体开裂而导致外部保温板撕裂的情况发生。本专利技术为一种抗裂粘接砂浆,在砂浆中加入一定量的乳液和纤维使粘接砂浆具有一定的柔性,在防止自身开裂的同时也会防止因墙体开裂导致的外层保温板开裂。具有广阔的应用前景。
技术实现思路
本专利技术涉及一种抗裂粘接砂浆,旨在解决普通粘接砂浆在因外界气温降低的情况下导致的容易开裂问题。本专利技术的技术方案如下所示:一种抗裂粘接砂浆,其配比由干料和外加剂构成;干料组成为水泥、粉煤灰、细沙,占比分别为,水泥25~30%,粉煤灰15~20%,细沙40~50%;外加剂组成为可分散性乳胶粉、聚丙烯、丙烯酸酯,占比分别为,可分散性乳胶粉0.15~0.20%,聚丙烯0.05~0.10%,丙烯酸酯0.05~0.1%;所述水泥为普通硅酸盐水泥,其强度等级为32.5;所述粉煤灰为一级粉煤灰;所述细沙为建筑用普通机制砂。本专利技术优点:采用等级强度为32.5的普通硅酸盐水泥作为胶凝材料,水化凝结速度快,早期强度和后期强度高,冻融性较好。粉煤灰占比大,减少了水泥的用量节约了资源,经济 ...
【技术保护点】
一种抗裂粘接砂浆,特征在于,其配比由干料和外加剂构成;干料组成为水泥、粉煤灰、细沙,占比分别为,水泥25~30%,粉煤灰15~20%,细沙40~50%;外加剂组成为可分散性乳胶粉、聚丙烯、丙烯酸酯,占比分别为,可分散性乳胶粉0.15~0.20%,聚丙烯0.05~0.10%,丙烯酸酯0.05~0.1%;所述水泥为普通硅酸盐水泥,其强度等级为32.5;所述粉煤灰为一级粉煤灰;所述细沙为建筑用普通机制砂。
【技术特征摘要】
1.一种抗裂粘接砂浆,特征在于,其配比由干料和外加剂构成;干料组成为水泥、粉煤灰、细沙,占比分别为,水泥25~30%,粉煤灰15~20%,细沙40~50%;外加剂组成为可分散性乳胶粉、聚丙烯、丙烯酸酯,...