The invention discloses a preparation method of the hot pressed melamine formaldehyde foam, which includes melamine, formaldehyde and alkaline catalyst to synthesize melamine formaldehyde resin. After mixing the melamine formaldehyde resin with emulsifier, curing agent, foaming agent and auxiliaries, the foam is made in the micro wave radiation field, so that the foam is made into foam. The non cured melamine formaldehyde foam was obtained. The hot press was used to hot press the non cured melamine formaldehyde foam directly to produce a hot press of melamine formaldehyde foam, thus greatly improving the toughness of melamine formaldehyde foam. It can be used in the main application field of the current melamine formaldehyde foam, the cleaning collar. Domain, and its decontamination capacity and life expectancy has a greater advantage.
【技术实现步骤摘要】
一种热压三聚氰胺甲醛泡沫的制备方法
本专利技术属于三聚氰胺泡沫的制备领域，具体涉及一种热压三聚氰胺甲醛泡沫的制备方法。
技术介绍
三聚氰胺泡沫是一种具有高开孔率、三维网络结构的新型泡沫塑料，具有十分优良的吸声性能、阻燃性能、隔热性能、吸水—保水性能、耐湿热稳定性及二次加工等性能，因而有十分广泛的应用领域。当前国内外已经有一些关于三聚氰胺甲醛泡沫的报道，但还很少见到有关针对其热压成型方面的研究，由于三聚氰胺甲醛泡沫本身的结构决定了它具有较好的刚性，但韧性方面仅仅依靠配方上的调整仍不能完全满足其在清洁领域的应用，以至于容易发生断裂而影响其使用效果。
技术实现思路
本专利技术的目的就在于为了解决上述问题而提供一种热压三聚氰胺甲醛泡沫的制备方法。本专利技术通过以下技术方案来实现上述目的：一种热压三聚氰胺甲醛泡沫的制备方法，包括：1)将三聚氰胺、甲醛、碱性催化剂合成三聚氰胺甲醛树脂；2)向三聚氰胺甲醛树脂中加入乳化剂、固化剂、发泡剂及助剂混匀后，在微波辐射场内进行发泡，使泡沫成型并得到未熟化的三聚氰胺甲醛泡沫；采用热压机直接对未熟化的三聚氰胺甲醛泡沫进行热压以制得热压三聚氰胺甲...
【技术保护点】
一种热压三聚氰胺甲醛泡沫的制备方法，包括：1)将三聚氰胺、甲醛、碱性催化剂合成三聚氰胺甲醛树脂；2)向三聚氰胺甲醛树脂中加入乳化剂、固化剂、发泡剂及助剂混匀后，在微波辐射场内进行发泡，使泡沫成型并得到未熟化的三聚氰胺甲醛泡沫；其特征在于，采用热压机直接对未熟化的三聚氰胺甲醛泡沫进行热压以制得热压三聚氰胺甲醛泡沫。
【技术特征摘要】
1.一种热压三聚氰胺甲醛泡沫的制备方法，包括：1)将三聚氰胺、甲醛、碱性催化剂合成三聚氰胺甲醛树脂；2)向三聚氰胺甲醛树脂中加入乳化剂、固化剂、发泡剂及助剂混匀后，在微波辐射场内进行发泡，使泡沫成型并得到未熟化的三聚氰胺甲醛泡沫；其特征在于，采用热压机直接对未熟化的三聚氰胺甲醛泡沫进行热压以制得热压三聚氰胺甲醛泡沫。2.根据权利要求1所述热压三聚氰胺甲醛泡沫的制备方法，其特征在于，对未熟化的三聚氰胺甲醛泡沫进行热压的过程包括以下步骤：1)确定待制造的热压三聚氰胺甲醛泡沫的厚度及顶面面积大小，利用泡沫切割机按照同样顶面面积大小、两倍厚...
【专利技术属性】
技术研发人员：张路，叶锐，刘铁，卢克涛，
申请(专利权)人：成都玉龙化工有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。