The invention discloses a concrete water reducing agent, which comprises a vinyl acetate ethylene copolymer powder, fatty acid soap, melamine formaldehyde resin of sodium silicate solution, which has good sphericity powder dispersed in aqueous solution and evenly dispersed in alkaline conditions, fatty acid soap as interface modification agent can make the dispersible powder surface properties change, the rubber powder surface and the adsorbed water molecules to form a water film, this film of water has a very good lubrication, and melamine formaldehyde resin has good hydrophilicity, can reduce agglomeration in water cement water reducing effect.
【技术实现步骤摘要】
一种水泥减水剂
本专利技术属于建材
，涉及一种水泥减水剂。技术背景近年来，混凝土在我国工程建设中发挥了重要作用。由于减水剂能有效地改善混凝土的性能，而且具有良好的经济效益，在许多国家都得到广泛应用，高效减水剂在工程中的应用越来越受到重视，成为混凝土中不可或缺的材料。减水剂经历了从木素磺酸盐、萘磺酸盐缩合物（奈系减水剂）、脂肪族及聚羧酸系等发展的历程，木素磺酸盐为最常用的普通减水剂，但该减水剂再搅拌过程中易造成缓凝，常引入大量空气而影响混凝土的性能；奈系减水剂在和成过程不可避免的硫酸钠含量的居高不下，进而导致外加剂中碱含量增高，混凝土的耐久性降低，众多工程出现碱骨料反应现象，使用寿命大幅缩短。此外，芳香族磺酸盐对人体和生物具有潜在的毒性。脂肪族减水剂生产所用的原材料甲醛丙酮等单体配比难以控制造成减水剂性能变差，与水泥基体产生相容性问题。现有聚羧酸减水剂成本高，合成过程中聚合度存在差异，使其性能存在差异；此外，我国砂石供需矛盾突出，天然砂逐渐被机制砂取代，然而机制砂在粒形，级配，表面质构以及0.075mm的石粉颗粒相比天然砂都有较大的区别，导致减水剂失效或减水效率下降，进而对混凝土性能产生重大影响。
技术实现思路
本专利技术的目的在于，克服现有技术的不足，提供了一种成本低、效率高的减水剂，本专利技术的减水剂减水率高、流动性好，可明显改善混凝土流动性和工作度，减水率可达20-30%。与混凝土有良好相容性，且对水泥混凝土的强度影响不大。为了解决上述技术问题，本专利技术所采取的技术方案如下：一种水泥减水剂，按照重量份数计它由以下组份组成：醋酸乙烯酯与乙烯共聚胶...
【技术保护点】
一种水泥减水剂，其特征在于按照重量份数计它由以下组份组成：醋酸乙烯酯与乙烯共聚胶粉20份，脂肪酸钾皂15份、三聚氰胺甲醛树脂15份、硅酸钠溶液20份。
【技术特征摘要】
1.一种水泥减水剂，其特征在于按照重量份数计它由以下组份组成：醋酸乙烯酯与乙...