Wire drawing process of titanium alloy seal

The invention discloses a titanium alloy seal strip drawing process. The titanium alloy rod is placed on the forming plate of the drawing mold, and the thickness of the forming plate in the drawing mold is adjusted according to the needs; the titanium alloy rod is extruded into the rectangular hole in the center of the forming plate, and the wire drawing is formed into a seal; the seal is obtained and the tolerance of the seal is within + 0.02mm. The invention adopts the drawing process to adjust the precision of the thickness of the forming plate in the drawing die, and control the tolerance of the forming seal within the positive and negative 0.02mm, and the tolerance can meet the process requirements of the vacuum brazing of the seal.

【技术实现步骤摘要】
钛合金封条拉丝工艺
：本专利技术属于钛合金封条成型
，特别涉及一种钛合金封条拉丝工艺。
技术介绍
：现有钛合金封条采用板材线切割工艺，钛板成型为冷轧工艺，执行GB/T3621标准，板幅越大，板公差越大，随着封条精度要求的增加，对板幅公差要求也越高，国标的板厚公差远远不能达到工艺需求。公开于该
技术介绍
部分的信息仅仅旨在增加对本专利技术的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
技术实现思路
：本专利技术的目的在于提供一种钛合金封条拉丝工艺，从而克服上述现有技术中的缺陷。为实现上述目的，本专利技术提供了一种钛合金封条拉丝工艺，其步骤为：(1)将钛合金棒放置拉丝成型模具成型板上；(2)根据需要调整拉丝成型模具中成型板的厚度；(3)对钛合金棒进行挤压，挤出的钛合金棒进入成型板中央的矩形孔内，拉丝成型为封条；(4)得到封条，封条公差在±0.02mm内。与现有技术相比，本专利技术具有如下有益效果：采用拉丝工艺，调整拉丝模具中成型板厚度的精度，将成型后的封条公差控制在正负0.02mm以内，公差小可满足封条真空钎焊的工艺要求。具体实施方式本文档来自技高网...

【技术保护点】
一种钛合金封条拉丝工艺，其步骤为：(1)将钛合金棒放置拉丝成型模具成型板上；(2)根据需要调整拉丝成型模具中成型板的厚度；(3)对钛合金棒进行挤压，挤出的钛合金棒进入成型板中央的矩形孔内，拉丝成型为封条；(4)得到封条，封条公差在±0.02mm内。

【技术特征摘要】
1.一种钛合金封条拉丝工艺，其步骤为：(1)将钛合金棒放置拉丝成型模具成型板上；(2)根据需要调整拉丝成型模具中成型板的厚度；...