一种氮化钛网纹辊及其制备方法技术

一种氮化钛网纹辊，由基辊、钛层以及氮化钛层组成，所述基辊上覆盖有钛层，所述钛层上覆盖有氮化钛层，所述钛层上设计有网孔，所述网孔呈U型，所述网孔阵型排列在钛层上。本发明专利技术的有益效果为：耐磨性能强，沉积率显著，可以局部修复，大大减少修复的工作量，且容易清洗掉油类、脂类等难清洗的物质，加工和使用的过程中无毒环保。

A titanium nitride reticulated roll and its preparation method

A titanium nitride reticle roller is composed of a base roll, a titanium layer and a titanium nitride layer. The base roll is covered with a titanium layer. The titanium layer is covered with titanium nitride layer. The titanium layer is designed with mesh holes, and the mesh holes are U. The mesh formation is arranged on the titanium layer. The beneficial effect of the invention is: strong wear resistance, significant deposition rate, local repair, greatly reducing the workload of repair, and easy cleaning of oil, lipids and other difficult to clean materials, processing and using the process of non-toxic and environmentally friendly.

【技术实现步骤摘要】
一种氮化钛网纹辊及其制备方法
本专利技术涉及一种网纹辊，具体涉及一种氮化钛网纹辊及其制备方法。
技术介绍
目前氧化铬陶瓷网纹辊虽然已经得到了大量的推广应用，但由于等离子喷涂氧化铬涂层本身的脆性造成其耐磨粒磨损性能较差，在一些使用环境中含有磨损颗粒的涂布或印刷应用中寿命较短。另外，等离子喷涂氧化铬涂层的孔隙率无法降得更低，抛光很难达到0.1的光洁度，致密性不够完美。现有的网纹辊耐磨性能方面还存在一定的不足，且网纹辊损伤的时候，需要整体进行重新喷涂才能修复，增加了工作量，网纹辊清洗也存在难度，清洗不干净，而影响印刷质量。
技术实现思路
本专利技术针对上述现有技术中的不足，提供一种氮化钛网纹辊及其制备方法，耐磨性能增强，易清洗，印刷效果精良，沉积率显著，且可以局部进行修复，降低成本且使用过程无毒环保。为实现上述目的，本专利技术采用如下技术方案：一种氮化钛网纹辊，由基辊、钛层以及氮化钛层组成，所述基辊上覆盖有钛层，所述钛层上覆盖有氮化钛层，所述钛层上设计有网孔。作为优选，所述网孔呈U型。作为优选，所述网孔阵型排列在钛层上。一种氮化钛网纹辊的制备方法，包括以下步骤：(1)将基辊面进行喷砂处理；(2本文档来自技高网...

【技术保护点】
一种氮化钛网纹辊，其特征在于：由基辊、钛层以及氮化钛层组成，所述基辊上覆盖有钛层，所述钛层上覆盖有氮化钛层，所述钛层上设计有网孔。

【技术特征摘要】
1.一种氮化钛网纹辊，其特征在于：由基辊、钛层以及氮化钛层组成，所述基辊上覆盖有钛层，所述钛层上覆盖有氮化钛层，所述钛层上设计有网孔。2.根据权利要求1所述一种氮化钛网纹辊，其特征在于：所述网孔呈U型。3.根据权利要求2所述一种氮化钛网纹辊，其特征在于：所述网孔阵型排列在钛层上。4.一种氮化钛网纹辊的制备方法，其特征在于：包括以下步骤：(1)将基辊面进行喷砂处理；(2)采用低压等离子喷涂系统在基辊面上喷涂钛涂层...