The invention provides a fluorine-containing silicone emulsion waterproof agent and preparation method thereof, which is made from the following raw materials by weight ratio of sodium fluosilicate: 20~30, ethylene vinyl acetate emulsion hydroxy silicone oil 10~18 copies, 30~38 copies, 2~8 copies of methyl cellulose, methyl methacrylate butyl six fluorine 10~20 copies, 50~80 copies of water. The fluorosilicone emulsion waterproofing agent has no toxic and harmful substances such as acetone, coal tar, etc., and has no organic solvent volatilization during construction, and is safe and environmental protection. The film has better aging resistance, weatherability and water resistance, and its preparation method can solve the problem of complex process and high cost. The invention is mainly applicable to the waterproof of industrial and living building materials, and can significantly prolong the service life of the materials.
【技术实现步骤摘要】
一种含氟硅乳液防水剂及其制备方法
本专利技术属于建筑节能环保涂料的生产领域，涉及一种建筑防水剂，具体涉及一种含氟硅乳液防水剂及其制备方法。
技术介绍
防水剂在目前的防水领域中占据了重要的地位，从小型建筑到大型工程的防水，它都不可或缺。将其涂刷在屋顶、地下室、卫生间、浴室或外墙等基层上，通过溶剂挥发、水分蒸发或反应固化后，可在常温条件下形成连续整体坚韧的，具有一定厚度的防水层。聚氨酯类防水剂时现在市场上常见的防水剂，这类材料一般是由聚氨脂与煤焦油作为原材料制成，它所挥发的焦油气毒性大，且不容易清除，因此于2000年在中国被禁止使用。尚在销售的聚氨脂防水剂，是用沥青代替煤焦油作为原料。但在使用这种防水剂时，一般采用含有甲苯、二甲苯等有机溶剂来稀释，因而也含有毒性。
技术实现思路
本专利技术的目的是提供一种含氟硅乳液防水剂及其制备方法，这种含氟硅乳液防水剂不含丙酮、煤焦油等有毒有害物质，绿色环保，本专利技术的制备方法可以解决工艺复杂，成本高的问题。本专利技术是通过如下技术方案实现的：一种含氟硅乳液防水剂，由下述按重量份配比计的原料制成：氟硅酸钠20～30份，乙烯-醋酸乙烯乳...
【技术保护点】
一种含氟硅乳液防水剂，其特征在于：它由下述按重量份配比计的原料制成：氟硅酸钠20～30份，乙烯‑醋酸乙烯乳液10～18份，羟基硅油30～38份，甲基纤维素2～8份，甲基丙烯酸六氟丁酯10～20份，水50～80份。
【技术特征摘要】
1.一种含氟硅乳液防水剂，其特征在于：它由下述按重量份配比计的原料制成：氟硅酸钠20～30份，乙烯-醋酸乙烯乳液10～18份，羟基硅油30～38份，甲基纤维素2～8份，甲基丙烯酸六氟丁酯10～20份，水50～80份。2.根据权利要求1所述的一种含氟硅乳液防水剂，其特征在于：它由下述按重量份配比计的原料制成：氟硅酸钠28份，乙烯-醋酸乙烯乳液15份，羟基硅油35份，甲基纤维素6份，甲基丙烯酸六氟丁酯18份，水60份。3.一种含氟硅乳液防水剂的制备方法，其特征在于，制备步骤如下：1)将水、羟基硅油和氟硅酸纳放入反应器中，逐步升温至75～85℃，搅拌20～30min，转速50～60r/min；2)往反应器中加入乙烯-...
【专利技术属性】
技术研发人员：黄志强，
申请(专利权)人：桂林市和鑫防水装饰材料有限公司，
类型：发明
国别省市：广西,45