一种二硫化钼气凝胶的制备方法技术

本发明专利技术公开了一种二硫化钼(MoS2)气凝胶的制备方法。该二硫化钼气凝胶的制备方法的制备特征包括：1)以四水合钼酸铵(分子式：(NH4)6Mo7O24·4H2O)为钼前驱体；2)以巯基丁二酸(分子式：C4H6O4S)为硫前驱体；3)以水为溶剂；4)以聚丙烯酸为添加剂；5)以环氧丙烷为凝胶促进剂；6)通过超临界干燥技术获得二硫化钼气凝胶。本发明专利技术的二硫化钼气凝胶的制备方法具有原料易得，工艺简单的特点。所制得的二硫化钼气凝胶的比表面积在200‑500m

A preparation method of molybdenum disulfide aerogel

The invention discloses a preparation method of molybdenum disulfide (MoS2) aerogel. The characteristics including the preparation method of the MoS2 aerogels: 1) to four hydrated ammonium molybdate (molecular formula: (NH4) 6Mo7O24 - 4H2O) Mo precursor; 2) with mercaptosuccinic acid (molecular formula: C4H6O4S) as sulfur precursor; 3) using water as solvent to 4); polyacrylic acid as additives; 5) with propylene oxide as gelation agent; 6) by supercritical drying technique of MoS2 aerogel. The preparation method of the molybdenum disulfide aerogel of the invention has the characteristics of easy raw material and simple process. Preparation of molybdenum disulfide aerogel of the specific surface area of 200 500m in

【技术实现步骤摘要】
一种二硫化钼气凝胶的制备方法
本专利技术属于气凝胶材料制备
，具体涉及一种制备二硫化钼气凝胶的方法。技术背景二硫化钼作为一种重要的硫化物材料，在固体润滑、微纳电子器件等方面有着重要的用途。尤其是近年来研究者们发现二硫化钼具有较高的电化学储能性能以及电分解水产氢的催化性能，可以用于高性能锂离子电池及光电化学电极材料。在上述的应用中，提高二硫化钼材料的比表面积以及优化其孔结构，对于增加具有电化学反应活性的表面位点，从而进一步提升材料性能有着极其重要的作用。气凝胶材料作为一种本征具有大比表面积和可控的孔结构的材料，在理论上可以满足以上的要求。因此，如果能够采用溶胶-凝胶工艺制备出二硫化钼气凝胶材料，对于进一步扩宽其在电化学储能和催化领域的有着重要的意义。在国内外的文献报道中，目前关于硫化钼(MoSx)气凝胶制备的方法主要可以分为两类：第一类是在2015年，Worsley等人直接以含硫的金属盐(成分为(NH4)2(MS4)，其中M为金属离子)为前驱体，通过冷冻干燥和后期在氢气中热处理的方法，制备了MoS2和WS2气凝胶，并研究了其作为吸附剂和电化学催化产氢催化剂的性能(ACSNan本文档来自技高网...

【技术保护点】
一种二硫化钼气凝胶的制备方法，其特征在于包含以下步骤：(1)以四水合钼酸铵为钼前驱体，水为溶剂，配置钼酸铵/水溶液，其中Mo

【技术特征摘要】
1.一种二硫化钼气凝胶的制备方法，其特征在于包含以下步骤：(1)以四水合钼酸铵为钼前驱体，水为溶剂，配置钼酸铵/水溶液，其中Mo6+的浓度为0.01M-1M；(2)以巯基丁二酸为硫前驱体，水为溶剂，配置巯基丁二酸/水溶液，其中巯基丁二酸的浓度为0.02M-2M；(3)将前述的钼源前驱体和硫前驱体混合，以体积比计算，钼前驱体溶液和巯基丁二酸溶液的比例在1:5-5:1之间；(4)在上述混合溶液中添加聚丙烯酸作为添加剂，添加量为溶液总体积的1-3％；(5)在上述溶液中滴加环氧丙烷作为凝胶促进剂，加入的体积量为溶液总体积的20-50％，获得溶胶；(6)将上述...

【专利技术属性】
技术研发人员：金一铭，金亚妮，支明佳，洪樟连，
申请(专利权)人：浙江大学，
类型：发明
国别省市：浙江,33