The invention relates to the technical field of the clutch, in particular to a high wear-resistant iron base powder metallurgy inner spline, a clutch cover and a clutch. Compared with the prior art, the invention relates to a high wear resistance of Fe based powder metallurgy inner spline according to weight percentage were divided into 0.35 graphite 2.25% copper, 0.8 2.8%, nickel 0.35 2.25%, Mn 0.8 3.25%, Cr 1.3 4.2%, 0.1 1.2% 0.1 niobium, titanium 1.2%, aluminum 0.1 0.7% rest for iron, and through mixing, pressing and sintering process is made, the internal spline and Aluminum Alloy hydraulic casting by integral molding with the inner spline clutch cover, and get through the clutch assembly, the internal spline, clutch cover clutch and good abrasion resistance, long service life, simple production process, while reducing the cost.
【技术实现步骤摘要】
一种高耐磨铁基粉末冶金内花键、离合器外罩及离合器
本专利技术涉及一种离合器
，特别是涉及一种高耐磨铁基粉末冶金内花键，和装配有该高耐磨铁基粉末冶金内花键的离合器外罩及离合器。
技术介绍
摩托车离合器是用于传递或切断发动机输出动力的关键部件。在离合器的结构中有一圆形外罩，用于设置内花键，该内花键与发动机的齿轮相配合，从而起到传递动力的作用，而传统使用的内花键是直接由铝合金制成，发动机功率和输出扭矩得不到提升，内花键承受的接触压力提高不了，使受到的摩擦磨损严重，生产过程使内花键尺寸精度无法保障，降低离合器的使用性能和寿命，在制作的过程中，工艺的繁琐性也会使成本增加。
技术实现思路
针对上述现有技术中的不足之处，本专利技术旨在提供一种高耐磨铁基粉末冶金内花键、离合器外罩及离合器，采用以铁为主要成分，添加石墨、铜、镍、铬等合金元素，保证其耐磨性能，并且使用节能、节材的粉末冶金工艺，使制作成本降低，在制作的过程中因为合金元素的加入导致基本不会产生液相，内花键的尺寸精度因此得到保障，采用该内花键制作的离合器外罩及离合器性能和使用寿命得到改善。为实现上述目的，本专利技术的技术...
【技术保护点】
一种高耐磨铁基粉末冶金内花键，其特征在于，按照重量百分比具有以下组分：石墨0.35‑2.25％，铜0.8‑2.8％，镍0.35‑2.25％，锰0.8‑3.25％，铬1.3‑4.2％，铌0.1‑1.2％，钛0.1‑1.2％，铝0.1‑0.7％，其余为铁。
【技术特征摘要】
1.一种高耐磨铁基粉末冶金内花键，其特征在于，按照重量百分比具有以下组分：石墨0.35-2.25％，铜0.8-2.8％，镍0.35-2.25％，锰0.8-3.25％，铬1.3-4.2％，铌0.1-1.2％，钛0.1-1.2％，铝0.1-0.7％，其余为铁。2.如权利要求1所述的一种高耐磨铁基粉末冶金内花键，其特征在于：按照重量百分比具有以下组分：石墨0.45-2.15％，铜0.95-2.7％，镍0.45-2.15％，锰0.95-3.15％，铬1.45-4.1％，铌0.15-1.15％，钛0.15-1.15％，铝0.15-0.65％，其余为铁。3.如权利要求1所述的一种高耐磨铁基粉末冶金内花键，其特征在于：按照重量百分比具有以下组分：石墨0.5-2.0％，铜1...
【专利技术属性】
技术研发人员：李毅，
申请(专利权)人：重庆译凌沛粉末冶金科技有限公司，
类型：发明
国别省市：重庆,50