The invention belongs to the technical field of powder metallurgy material production, in particular to a novel powder metallurgy material and a preparation method thereof. The utility model is characterized in that: a new type of powder metallurgy material and its preparation method, 80-100 by weight of iron powder is composed of 99-101, 0.8-1.2 0.6-1.0 in paraffin granular graphite, automatic temperature control heating mixing device, mixing temperature at 79-81 degrees 45-60 minutes, and then fully mixed powder removed after cooling to room temperature. The utility model has the advantages of uniform composition, stable product quality, low cost and no pollution to the environment.
【技术实现步骤摘要】
:本专利技术属粉末冶金材料生产
,具体涉及一种新型粉末冶金材料及其制备方法。
技术介绍
:目前,粉末冶金大都是在铁粉中加入硬脂酸锌和石墨,通过专用机械混料机,在常温下长时间混合制得粉末压制用的粉料。其中硬脂酸锌在材料中只是润滑剂,作用是减少粉末颗粒之间和它与模具之间压制时的摩擦力,而且硬脂酸锌在制品烧结工序时需全部去除,其存在问题一是:硬脂酸锌粉末和石墨粉与铁粉的比重相差很大,用机械的方式混合,存在混合后成分不均匀和制品压制后成份偏析的现象,致使压制产品质量不稳定,影响制品的机械性能;二是在混料和产品压制过程中,作业环境有较多粉尘,易造成环境污染;三是在制品的烧结工序中,硬脂酸锌熔点在120℃左右,去除它很不方便,且烧结升温速度快,产品易起泡易导致报废,造成一定浪费;四是烧结过程中,硬脂酸锌挥发物严重污染炉膛,在炉膛内壁上短时间形成厚的坚硬结垢,必须停炉清除,且清除干净非常困难,严重影响正常生产和烧结炉马弗的寿命。
技术实现思路
:本专利技术的目的是提供一种成分均匀,产品质量稳定,成本低,对环境无污染的新型粉末冶金材料及其制备方法。本专利技术的技术方案是:一种新型粉末冶金材料,其特征是由以下组份按重量份组成:80-100目铁粉99-101,颗粒状石蜡0.8-1.2,石墨0.6-1.0。一种新型粉末冶金材料的制备方法,其特征是包括以下工艺步骤:将上述成份放入自动控温加热的混料设备内,温度在79-81℃下混合45-60分钟,再将充分混合的粉末取出后冷却至室温即可。由于采用上述技术方案,用颗粒状石蜡代替了硬脂酸锌,混料温度为79-81℃,而石蜡熔点为60℃左 ...
【技术保护点】
一种新型粉末冶金材料,其特征是由以下组份按重量份组成:80‑100目铁粉99‑101,颗粒状石蜡0.8‑1.2,石墨0.6‑1.0。
【技术特征摘要】
1.一种新型粉末冶金材料,其特征是由以下组份按重量份组成:80-100目铁粉99-101,颗粒状石蜡0.8-1.2,石墨0.6-1.0。2.一种新型粉末冶金材...
【专利技术属性】
技术研发人员:王乐进,
申请(专利权)人:龙口精益工贸有限公司,
类型:发明
国别省市:山东;37