The invention discloses a high tensile strength of ABS composite material and preparation method thereof, which comprises the following parts by weight of raw material preparation: 6 nano glass fiber, 15 copies of 10 copies of the 5 modifier, 10 15 copies of the 55 75 styrene butadiene rubber, ABS resin, 1 coupling the 0.3 agent, 3 copies of 0.6 copies of the crosslinking agent; the invention will pass for nano glass fiber and ABS resin by modification of the composite, and the nano glass fiber is uniformly dispersed in ABS resin, ABS composite material with high tensile strength and excellent performance, is conducive to the application of ABS resin in more areas in.
【技术实现步骤摘要】
一种高拉伸强度ABS复合材料及其制备方法
本专利技术涉及改性材料领域，具体涉及一种高拉伸强度ABS复合材料及其制备方法。
技术介绍
ABS树脂是由丙烯腈、丁二烯和苯乙烯组成的三元共聚物，因为其抗冲击性、耐热性、耐低温性、耐化学药品性及电气性能优良，还具有易加工、制品尺寸稳定、表面光泽性好等特点，容易涂装、着色，还可以进行表面喷镀金属、电镀、焊接、热压和粘接等二次加工，广泛应用于机械、汽车、电子电器、仪器仪表、纺织和建筑等工业领域。随着人们对材料拉伸性能要求的不断提高，未经拉伸增强改性的ABS树脂已难以满足需求，因而，对ABS树脂进行拉伸增强改性成为必要。现今对ABS的拉伸增强改性处理方法种类繁多，改性效果也很好，尤其是随着纳米材料的出现和应用，ABS树脂的拉伸强度增加效果显著，使ABS树脂能在更多领域大量使用，但也存在不足。纳米材料虽然具有拉伸强度增强效果好，添加量小的优点，但也存在分散困难，成本高等缺陷。在进行拉伸强度改性过程中，纳米材料分散不均会影响其拉伸增强效果，得到的改性材料拉伸强度偏低，对改性材料的生产和应用造成不利影响。
技术实现思路
本专利技术的目的在于...
【技术保护点】
一种高拉伸强度ABS复合材料，其特征在于，包括以下重量份原材料制备得到：6‑15份的纳米玻璃纤维、5‑10份的改性剂、10‑15份的丁苯橡胶、55‑75份的ABS树脂、1‑3份的偶联剂、0.3‑0.6份的交联剂；所述改性剂为正硅酸甲酯与磷酸三甲酯组成的混合物；所述偶联剂为乙烯基硅烷偶联剂，所述交联剂为过氧化二异丙苯；所述丁苯橡胶的聚合度为220‑340；所述ABS树脂聚合度为800‑1600。
【技术特征摘要】
1.一种高拉伸强度ABS复合材料，其特征在于，包括以下重量份原材料制备得到：6-15份的纳米玻璃纤维、5-10份的改性剂、10-15份的丁苯橡胶、55-75份的ABS树脂、1-3份的偶联剂、0.3-0.6份的交联剂；所述改性剂为正硅酸甲酯与磷酸三甲酯组成的混合物；所述偶联剂为乙烯基硅烷偶联剂，所述交联剂为过氧化二异丙苯；所述丁苯橡胶的聚合度为220-340；所述ABS树脂聚合度为800-1600。2.根据权利要求1所述的ABS复合材料，其特征在于，所述改性剂中正硅酸甲酯与磷酸三甲酯的物质的量之比为1︰1。3.根据权利要求1所述的ABS复合材料，其特征在于，所述丁苯橡胶的聚合度为260-300。4.根据权利要求3所述的ABS复合材料，其特征在于，所述丁苯橡胶的聚合度为280。5.根据权利要求1所述的ABS复合材料，其特征在于，所述A...
【专利技术属性】
技术研发人员：舒春柳，
申请(专利权)人：四川力智久创知识产权运营有限公司，
类型：发明
国别省市：四川,51