A preparation method for deep profile control agent with weak gel

The invention relates to the technical field of fine oil processing, in particular to a preparation method of a weak gel deep profile control agent. A preparation method of weak gel deep profile control agent includes the following steps: Step 1: raw material preparation; step 2: preparation of polymer main agent; step 3: preparation of crosslinking agent. The method provided by the invention is simple and easy to operate, and the experimental condition is easy to achieve. The weak gel prepared by the method provided by this invention has higher viscosity and suitable gelation time, and it can be used for deep profile control.

【技术实现步骤摘要】
一种弱凝胶深部调剖剂的制备方法
本专利技术涉及精细石油加工
，具体涉及一种弱凝胶深部调剖剂的制备方法。
技术介绍
交联聚合物驱可充分发挥交联聚合物的优势，实现高注入能力和大规模注入，对油藏内部流体起到调节作用。交联聚合物驱不仅能起到调剖、堵水的作用，同时能调节层间或层内矛盾，增加波及体积。按聚合物使用浓度分类，交联聚合物可分为2种：一是胶态分散凝胶或可流动凝胶等低浓度聚合物体系；二是弱凝胶调驱体系。弱凝胶是一种由低浓度聚合物和交联剂形成的凝胶体系，可大幅度降低化学剂用量。大量研究表明，弱凝胶或胶态分散凝胶(CDG)深部调剖技术经济可行，具有较好的应用前景。
技术实现思路
本专利技术旨在提出一种弱凝胶深部调剖剂的制备方法。本专利技术的技术方案在于：一种弱凝胶深部调剖剂的制备方法，包括以下步骤：步骤1：原材料制备：乳酸钠，结晶氯化铝，柠檬酸三钠，乙酸钠，硫脲，聚丙烯酰胺；步骤2：聚合物主剂的配制：称取聚丙烯酰胺粉末，配制聚丙烯酰胺溶液母液，并将配制好的母液稀释；步骤3：交联剂的制备：（1）分别称取25g柠檬酸三钠、乙酸钠、乳酸钠和氯化铝，加蒸馏水分别溶解在烧杯中，并分别移人250mL的本文档来自技高网...

【技术保护点】
一种弱凝胶深部调剖剂的制备方法，其特征在于：包括以下步骤：步骤1：原材料制备：乳酸钠，结晶氯化铝，柠檬酸三钠，乙酸钠，硫脲，聚丙烯酰胺；步骤2：聚合物主剂的配制：称取聚丙烯酰胺粉末，配制聚丙烯酰胺溶液母液，并将配制好的母液稀释；步骤3：交联剂的制备：（1）分别称取25g柠檬酸三钠、乙酸钠、乳酸钠和氯化铝，加蒸馏水分别溶解在烧杯中，并分别移人250 mL的容量瓶中，配制成10％的盐溶液；（2）按物质的量比为1：1将氯化铝分别与柠檬酸三钠、乙酸钠和乳酸钠配制成交联剂。

【技术特征摘要】
1.一种弱凝胶深部调剖剂的制备方法，其特征在于：包括以下步骤：步骤1：原材料制备：乳酸钠，结晶氯化铝，柠檬酸三钠，乙酸钠，硫脲，聚丙烯酰胺；步骤2：聚合物主剂的配制：称取聚丙烯酰胺粉末，配制聚丙烯酰胺溶液母液，并将配制好的母液稀释；步骤3：交联剂的制备：（1）分别称取25g柠檬酸三钠、乙酸钠、乳酸钠和氯化铝，加蒸馏水分别溶解在烧杯中...