本发明专利技术公开一种熔融制备热塑性壳聚糖的加工方法，所述方法以一定粘度、一定脱乙酰度的壳聚糖，少量稀酸溶液为原料，按照一定质量比混合，然后在加工设备如密炼机中混炼即可。本发明专利技术方法制备过程简单，工艺条件可控性强，材料结构和性能容易控制；本发明专利技术所制备的材料是一种固相的热塑性材料，可以在不需要处理（如干燥或添加其它增塑剂）的条件下直接二次成型。本发明专利技术可以为壳聚糖材料的制备提供一种大量且连续化生产的加工方法。

Melting processing method for preparing thermoplastic chitosan

The processing method of the invention discloses a molten thermoplastic preparation of chitosan, the method with a certain viscosity, a certain degree of deacetylation of chitosan, a dilute acid solution as the raw material, according to a certain ratio, and then mixing the processing equipment such as mixer. The method of the invention has the advantages of simple preparation process conditions, strong controllability, easy to control the structure and properties of materials; the prepared material is a solid thermoplastic material, can not need to deal with (such as drying or adding other plasticizers) under the condition of two direct molding. The invention can provide a large number of continuous processing methods for preparing chitosan materials.

【技术实现步骤摘要】
一种制备热塑性壳聚糖的熔融加工方法
本专利技术涉及高分子材料领域以及天然高分子材料领域，具体涉及一种制备热塑性壳聚糖的熔融加工方法。
技术介绍
利用可再生植物资源为原料，对其进行改性来制备可生物降解材料，不仅可以节约石油资源，保护环境，还可以提高农副产品的附加值。壳聚糖是一种环境友好的天然高分子材料，其产量丰富，价格低廉。壳聚糖含有氨基,是天然多糖中唯一含氮的碱性多糖。凭借独特的抑菌作用、优越的成膜性和生物相容性,壳聚糖基复合材料在食品包装和保鲜方面有着极大的应用前景。由于壳聚糖自身的分解温度低于熔融温度，所以壳聚糖不能熔融加工，目前制备壳聚糖膜材料使用的方法都是将壳聚糖溶解在稀酸或离子溶液中，然后再进行改性或共混。例如一种比较通用的制备壳聚糖膜的方法是取一定质量的壳聚糖，溶解于2％(v/v)醋酸水溶液中配成5％(w/v)浓度的壳聚糖溶液，在一定温度的烘箱中恒温静置脱泡1h后在玻璃板上流延成膜，将制成的膜在60℃下干燥除去溶剂，然后用5％KOH水溶液处理，最后水洗干燥得到壳聚糖膜。对于壳聚糖基复合材料的制备，目前也使用的是类似的方法。Xu等人将壳聚糖溶于1％的乳酸溶液中，配制成2％的本文档来自技高网...

【技术保护点】
一种制备热塑性壳聚糖的熔融加工方法，包括：将脱乙酰度≥80%，分子量5‑20万的壳聚糖与酸溶液进行混合，然后置于密炼机中进行密炼，密炼温度为60℃‑90℃，密炼时间为10‑15min，密炼转速20‑35rpm；所述的酸溶液中酸的质量分数6%‑80%，壳聚糖与酸溶液的质量比为1：1.2‑2.0；所述的酸溶液中的酸为可以溶解壳聚糖的酸。

【技术特征摘要】
1.一种制备热塑性壳聚糖的熔融加工方法，包括：将脱乙酰度≥80%，分子量5-20万的壳聚糖与酸溶液进行混合，然后置于密炼机中进行密炼，密炼温度为60℃-90℃，密炼时间为10-15min，密炼转速20-35rpm；所述的酸溶液中酸的质量分数6%-80%，壳聚糖与酸溶液的质量比为1：1.2-2.0；所...

【专利技术属性】
技术研发人员：冯继文，张宇，
申请(专利权)人：中国科学院武汉物理与数学研究所，
类型：发明
国别省市：湖北,42