The present invention relates to a production process for colored flame retardant antibacterial cellulose fiber dope for the purpose of preparing a dissolving pulp or cotton pulp as raw material, with colored flame retardant antibacterial cellulose fiber, its raw material and the weight percentage is: dissolving wood pulp cellulose 90 alpha 93, water 8 10. The production process of the pulp into the temperature of 52 DEG C impregnation solution; alkali cellulose press after crushing, aging, temperature is 52 DEG C 54 DEG C; carbon disulfide is 32% 34% adding amount of alphacellulose, yellow for 30 minutes or so, the temperature of 18 DEG 30 DEG C; dissolved in alkali solution the dissolution, filtration, deaeration, spinning syringe adding flame retardant, inorganic pigment paste and antibacterial agent, flame retardant or a fiber weight fraction is 20%, the antibacterial agent or a fiber weight fraction is 2 5%, accounting for a 3 weight fraction of fiber paste 5%.
【技术实现步骤摘要】
有色阻燃抗菌纤维素纤维原液的制备
本专利技术涉及一种有色阻燃抗菌纤维素纤维原液的制备。
技术介绍
纤维素纤维有其它合成纤维所不具有的优异性能，但是存在下游企业在染整时高污染、高能耗以及染料利用率低的情况，同时纤维素纤维本身属于易燃纤维，在常规纤维素纤维制备原液中加入耐碱、耐酸的无机颜料以及阻燃剂和抗菌剂制备具有多功能纤维素纤维原液是本专利技术的主要目的。
技术实现思路
本专利技术的目的是制备一种以溶解浆粕或者棉浆粕为原料，具有有色阻燃抗菌功能的纤维素纤维，在纺丝过程中，采用纺前注射设备将含有无机色浆、阻燃剂浆料和抗菌剂浆液均匀注入纺丝管中经纺丝制备阻燃无光高白纤维素纤维原液。一种有色阻燃抗菌纤维素纤维原液的生产方法，它包括下列步骤：（a）浸渍：将浆粕放入，温度：52℃，时间：30-35分钟，碱的浓度：220g/L，V-388用量：0.03%-0.10%（相对于甲纤）；（b）压榨：将原料用压榨机压榨粉碎，定积重110-160克/升；（c）老成：将粉碎后的原料老成，温度49-60℃，老成出口铜氨粘度50mp；（d）黄化：二硫化碳对甲纤加入量32-35%，黄化时间为25-3...
【技术保护点】
一种有色阻燃抗菌纤维素纤维原液的制备。
【技术特征摘要】
1.一种有色阻燃抗菌纤维素纤维原液的制备。2.一种制造权利要求书1所述的有色阻燃抗菌纤维素纤维原液的生产工艺，其工艺要求包括下列步骤：（a）浸渍：将浆粕放入，温度：52℃，时间：30-35分钟，碱的浓度：220g/L，V-388用量：0.03%-0.10%（相对于甲纤）；（b）压榨：将原料用压榨机压榨粉碎，定积重110-160克/升；（...
【专利技术属性】
技术研发人员：李锡泉，桑海军，周琳琳，
申请(专利权)人：山东雅美科技有限公司，
类型：发明
国别省市：山东,37