The invention provides a steel surface spraying process, which comprises the following steps: A, cleaning, removal of impurities on the surface; B, cleaning and drying, high-pressure water washing and drying; C, spraying insulation layer, the steel surface drying after spraying insulating layer, the insulating layer thickness of 20 30 m; D, spraying oxidation layer, spraying layer based on antioxidant insulating layer, the oxidation layer thickness of 30 50 m; E, spraying corrosion layer, spraying corrosion layer based on anti oxidation layer on the corrosion layer thickness of 50 F, 80 m; vacuum cooling, cooling to room temperature. The steel surface spraying process of the invention is convenient and quick, and the steel is not easily oxidized or corroded, and the service life of the steel is greatly improved.
【技术实现步骤摘要】
一种钢材表面喷涂工艺
本专利技术涉及一种金属表面喷涂工艺，特别涉及一种钢材表面喷涂工艺。
技术介绍
钢材在日常生活随处可见，钢材应用广泛、品种繁多。由于其特定的工作环境，经过日夜的风吹雨打，刚刚容易被腐蚀或者生锈。现有技术中针对钢材表面的生锈或腐蚀的问题处理方式是表面涂油漆，这样方式带来的弊端在于钢材使用寿命不长。
技术实现思路
【1】要解决的技术问题本专利技术要解决的技术问题是提供一种加工方便快捷，钢材不易被氧化或腐蚀的钢材表面喷涂工艺。【2】解决问题的技术方案本专利技术提供钢材表面喷涂工艺，其包括以下步骤：a、去杂，去除表面的杂质；b、清洗并烘干，高压水枪冲洗并烘干；c、喷涂绝缘层，将烘干后的钢材表面喷涂绝缘层，所述绝缘层的厚度为20-30μm；d、喷涂抗氧化层，在绝缘层的基础上喷涂抗氧化层，所述抗氧化层的厚度30-50μm；e、喷涂耐腐蚀层，在抗氧化层的基础上喷涂耐腐蚀层，所述耐腐蚀层的厚度为50-80μm；f、冷却，真空冷却至室温。进一步的，喷涂选用的设备为等离子喷涂机。【3】有益效果本专利技术钢材表面喷涂工艺，加工方便快捷，钢材不易被氧化或腐蚀，大大的提高了...
【技术保护点】
一种钢材表面喷涂工艺，其特征在于，包括以下步骤：a、去杂，去除表面的杂质；b、清洗并烘干，高压水枪冲洗并烘干；c、喷涂绝缘层，将烘干后的钢材表面喷涂绝缘层，所述绝缘层的厚度为20‑30μm；d、喷涂抗氧化层，在绝缘层的基础上喷涂抗氧化层，所述抗氧化层的厚度30‑50μm；e、喷涂耐腐蚀层，在抗氧化层的基础上喷涂耐腐蚀层，所述耐腐蚀层的厚度为50‑80μm；f、冷却，真空冷却至室温。
【技术特征摘要】
1.一种钢材表面喷涂工艺，其特征在于，包括以下步骤：a、去杂，去除表面的杂质；b、清洗并烘干，高压水枪冲洗并烘干；c、喷涂绝缘层，将烘干后的钢材表面喷涂绝缘层，所述绝缘层的厚度为20-30μm；d、喷涂抗氧化层，在绝缘层的基础上喷涂抗氧...