本发明专利技术公开了一种稳定辊堆焊钴基合金工作面，设置在稳定辊辊筒外壁上，堆焊两层以上；所采用的钴基合金堆焊材料的成分以重量百分比计为：10％‑15％的Cr、10％‑15％的Ni、0.3％‑0.5％的V、0.3％‑0.5％的Ti、1.2％‑1.5％的C、15％‑20％的Fe、4.0％‑5.0％的Al、2.0％‑3.0％的Mo、4.0％‑5.0％的Nb、2.0％‑3.0％的Si、0.06％‑0.10％的RE，其余为Co和不可避免的杂质。本发明专利技术显著细化钴基合金工作面的结晶组织，从而显著提高本发明专利技术的综合性能，特别是高温耐磨性能和抗热裂变性能。

Stable roll surfacing of cobalt base alloy working face

The invention discloses a stable roller surfacing cobalt based alloy surface, stable roller arranged in the outer wall, surfacing layer two above; cobalt based alloy surfacing materials used by the components by weight percentage: 10% 15% Cr, 10% Ni, 0.3% 15% 0.5% V, 0.3% 0.5% Ti, 1.2% C, 15% 1.5% 20% Fe, 4% Al, 2% 5% 3% Mo, 4% Nb, 2% 5% 3% Si, 0.06% 0.10% RE, other Co and inevitable impurities. The invention significantly refines the crystalline structure of the cobalt base alloy working face, thereby significantly improving the comprehensive performance of the invention, especially the high temperature wear resistance and thermal cracking resistance.

【技术实现步骤摘要】
稳定辊堆焊钴基合金工作面
本专利技术涉及一种金属表面层，具体涉及一种稳定辊表面层。
技术介绍
稳定辊浸没在装有锌铝合金熔液的热镀锌铝锅中，并在450-550℃温度范围内工作，需要其工作表面具有较高的高温耐磨性能和抗热裂变性能，现有稳定辊工作表面的高温耐磨性能和抗热裂变性能较差。
技术实现思路
本专利技术针对现有技术的不足，提出一种能显著提高高温耐磨性能和抗热裂变性能的稳定辊堆焊钴基合金工作面。本专利技术通过下述技术方案实现技术目标。稳定辊堆焊钴基合金工作面，设置在稳定辊辊筒外壁上，其改进之处在于：堆焊两层以上；所采用的钴基合金堆焊材料的成分以重量百分比计为：10％-15％的Cr、10％-15％的Ni、0.3％-0.5％的V、0.3％-0.5％的Ti、1.2％-1.5％的C、15％-20％的Fe、4.0％-5.0％的Al、2.0％-3.0％的Mo、4.0％-5.0％的Nb、2.0％-3.0％的Si、0.06％-0.10％的RE，其余为Co和不可避免的杂质。本专利技术与现有技术相比，具有以下积极效果：加入大量的稀土元素RE，显著细化钴基合金工作面的结晶组织，从而显著提高本专利技术的综合性能，本文档来自技高网...

【技术保护点】
一种稳定辊堆焊钴基合金工作面，设置在稳定辊辊筒外壁上，其特征在于：堆焊两层以上；所采用的钴基合金堆焊材料的成分以重量百分比计为：10％‑15％的Cr、10％‑15％的Ni、0.3％‑0.5％的V、0.3％‑0.5％的Ti、1.2％‑1.5％的C、15％‑20％的Fe、4.0％‑5.0％的Al、2.0％‑3.0％的Mo、4.0％‑5.0％的Nb、2.0％‑3.0％的Si、0.06％‑0.10％的RE，其余为Co和不可避免的杂质。