The invention discloses a semiconductor laser cladding of Ni based alloy powder repair centrifugal milling pipe mould for inner wall, which belongs to the laser cladding, nickel based alloy powder for the C:0.06 0.09% according to weight percentage, Cr:20 22%, B:0.5 1%, Fe:2 6%, Mo:8 10%, Al:4 8%, W:0.6 1.2%, Nb+Ta:2 6%, the rest is Ni; the nickel based alloy powder for laser cladding alloy powders for the laser diode 800nm to 1000nm wavelength, the cladding layer has a high impact performance at the same time, has good resistance to thermal fatigue; in ductile iron pipes under the condition, can effectively improve the thermal fatigue the performance of laser cladding layer function; the powder on the inside wall of the pipe mould overall laser cladding repair, can prolong the service life, greatly reduce production costs, improve economic efficiency.
【技术实现步骤摘要】
一种用于修复离心球磨管模内壁的半导体激光熔覆镍基合金粉末
本专利技术涉及激光表面熔覆技术，尤其涉及一种用于修复离心球磨铸管管模内壁的具有高冲击韧性、抗热疲劳特性的半导体激光熔覆镍基合金粉末。
技术介绍
离心球墨铸管管模是制造离心球墨铸铁管的关键部件，在离心铸造球墨铸铁管的制造成本中占有很高的比例，其制造成本昂贵，尤其是大直径铸管模，经过上千次使用后，由于热疲劳磨损失效，造成巨大的浪费。管模反复进行使用磨损和维修引起管模的内表面尺寸出现超差，以及管模内表面出现无法维修的缺陷，如管模中间出现龟裂纹等，都会导致管模无法继续使用。从管模失效样品的失效形式来看，主要是热裂。裂纹呈网格状、均匀、没有明显的方向性，经打磨无氧化皮，可以判断失效的主要原因在于热疲劳和应力所造成的热裂。热应力是造成管模损坏的主要原因，管模产生热应力主要有以下两点：一是管模壁热膨胀或冷收缩受到相邻材料的约束；二是管壁热循环过程产生热冲击。对于管模来说，其冲击韧性性能和组织状态决定管模的使用寿命的长短。对管模内壁修复来说，传统的修复方式即堆焊，一方面由于受管模内孔尺寸的限制，焊接机头的深入，焊丝，焊剂的...
【技术保护点】
一种用于修复离心球磨管模内壁的半导体激光熔覆镍基合金粉末，其特征在于，所述的镍基合金粉末按照重量百分比为C：0.06‑0.09%，Cr：20‑22%，B：0.5‑1.0%，Fe：2‑6%，Mo：8‑10%，Al：4‑8%，W：0.6‑1.2%，Nb+Ta：2‑6%，其余为Ni。
【技术特征摘要】
1.一种用于修复离心球磨管模内壁的半导体激光熔覆镍基合金粉末，其特征在于，所述的镍基合金粉末按照重量百分比为C：0.06-0.09%，Cr：20-22%，B：0.5-1.0%，Fe：2-6%，Mo：8-10%，Al：4-8%，W：0.6-1.2%，Nb+Ta：2-6%，其余为Ni。2.根据权利要求1所述的一种用于修复离心球磨管模内壁的半导体激光熔覆镍基合金粉末，其特征在于，所述的镍基合金粉末按照重量百分比为：C：0.08%，Cr：21%，B：1%，Fe：5%，Mo：9%，Al：5%，W：1%，Nb+Ta：4%，其余为Ni。3.根据权利要求1或2所述的一种用于修复离心球磨管模内壁的半导体激光熔覆镍基合金粉末，其特征在于，所述的镍基合金粉末的目...
【专利技术属性】
技术研发人员：姜涵之，李文斌，
申请(专利权)人：山西鑫盛激光技术发展有限公司，
类型：发明
国别省市：山西,14