The invention discloses a forging process for titanium alloy taper sleeve, and sequentially includes heating technology, band sawing, making round billets, expanding holes, forging and shaping, annealing, lathe processing and inspection. Through a series of processing by the process, finally made the forging of titanium alloy taper sleeve greatly improves the quality, but also shorten the duration of forging of titanium alloy, expanding the taper sleeve using group, improve the rate of finished products from raw materials to finished products, which saves raw materials, reduces the cost for forging. The promotion and use of the taper sleeve, by setting the heating temperature and deformation rate control in forging process and forging the order and direction, can effectively shape the taper sleeve shape, improve the quality of forging taper sleeve.
【技术实现步骤摘要】
一种钛合金锥度套的锻造工艺
本专利技术属于锥度套的锻造
，特别是涉及一种钛合金锥度套的锻造处理工艺。
技术介绍
钛合金锥度套是一种新型机械传动联接部件，具有标准化程度高、精度高、结构紧凑、安装拆卸方便等特点，适用于各种场合，锻造尺寸为Φ572±5×Φ242±5×380±5，但从原料上来说投料重量393.5kg+390kg，总投料为783.5kg,而成品重量是161kg,成品率只有20.6%，从机械加工方面来说，加长了加工周期，加工1件零件需要回转直径80以上的车床才能满足加工能力，而且加工时间需要10天，加工时间太长，传统油压机吨位在1600吨或1600吨以上才能锻造。否则锻透性不好，会造成超声波探伤及力学性能不合格，合成本相当高，按目前市场价原材料成本在66597元，锻造费在23505元，机械加工费在16897元，总成本在：106999元，平均1件的成本在：53499.5元，总之传统锻造方法成本高、周期长，在市场上很难推广，费用较高。
技术实现思路
本专利技术的所要解决的技术问题是提供一种加工工期短、成本较低以及使用群体广泛的钛合金锥度套锻造工艺，它具有应用范...
【技术保护点】
一种钛合金锥度套的锻造工艺，其特征在于：沿处理顺序依次包括以下步骤：加热、带锯中分、圆坯制作、扩孔、锻造整形、退火、车床加工、检查。
【技术特征摘要】
1.一种钛合金锥度套的锻造工艺，其特征在于：沿处理顺序依次包括以下步骤：加热、带锯中分、圆坯制作、扩孔、锻造整形、退火、车床加工、检查。2.根据权利要求1所述的一种钛合金锥度套的锻造工艺，其特征在于：所述加热步骤具体为，用电炉加热至1100-1190℃，并保温230-300分钟，先将锥度套拔长，再做两鐓两拔到270的方，将其打磨干净。3.根据权利要求1所述的一种钛合金锥度套的锻造工艺，其特征在于：所述带锯中分步骤具体为，带锯中分，单重约147kg/共2件。4.根据权利要求1所述的一种钛合金锥度套的锻造工艺，其特征在于：所述圆坯制作步骤具体为，电炉加热930-1000℃，保温170-220分钟，做两鐓两拔到300的圆坯，回火60分钟，冲孔，打磨干净，锻造制坯后，尺寸为Φ350±5×Φ145+5×400±5。5.根据权利要求1所述的一种钛合金锥度套的锻造工艺，其特征在于：所述扩孔步骤具体为电炉加热930-1000℃，保温170-220分钟，上马架扩孔，在马架上扩孔时，先扩操作机夹...
【专利技术属性】
技术研发人员：刘永开，
申请(专利权)人：宝鸡市紫玉金属材料有限公司，
类型：发明
国别省市：陕西,61