The present invention discloses a kind of modified calcium carbonate and preparation method and application thereof. The preparation method of modified calcium carbonate, which comprises the following steps: (1) of the 20~26 buffer solution of calcium carbonate powder impregnated with weak alkaline in hours, and then filtered to remove water, under vacuum drying, 55~65 C 10~14 h; (2) then take steps (1) the product of less than 600 milled into powder, in the milling process, adding silane coupling agent containing amino type urea groups, modified calcium carbonate can be obtained by the. The modified calcium carbonate can be used as an additive to prepare the chlorinated polyvinyl chloride compound. The modified calcium carbonate can improve the compatibility of chlorinated polyvinyl chloride mixture, maintain its processing stability, maintain its original physical property and reduce its cost.
【技术实现步骤摘要】
改性碳酸钙及其制备方法和应用
本专利技术涉及用于氯化聚氯乙烯加工(CPVC)的改性碳酸钙。
技术介绍
氯化聚氯乙烯(CPVC)树脂是由PVC树脂氯化而成，其含氯量最高可达73.2％，一般为63～68％。由于在氯乙烯链中引入了氯，故随着氯含量的增加，使树脂分子间的作用力增强，从而提高了树脂的软化温度和机械性能，氯化聚氯乙烯的玻璃化温度比通用聚氯乙烯的玻璃化温度高50℃左右，软化点也比聚氯乙烯高，可在100℃左右长期使用。并且随着氯化度的提高，软化点及耐热性也随之上升。由于CPVC在耐热性、耐蚀性、耐老化性及阻燃自熄性方面远优于PVC树脂，其应用范围要广泛得多。碳酸钙是一种无机化合物，俗称：灰石、石灰石、石粉、大理石等。主要成分：方解石，化学式是CaCO，呈中性，基本上不溶于水，溶于盐酸。它是地球上常见物质，存在于霰石、方解石、白垩、石灰岩、大理石、石灰华等岩石内，亦为动物骨骼或外壳的主要成分。碳酸钙是重要的建筑材料，工业上用途甚广。根据碳酸钙生产方法的不同，可以将碳酸钙分为重质碳酸钙、轻质碳酸钙、胶体碳酸钙和晶体碳酸钙。其中在塑料填料领域主要使用重质碳酸钙和轻质碳酸...
【技术保护点】
改性碳酸钙的制备方法，其特征在于，包括如下步骤：(1)将碳酸钙粉末浸渍于弱碱性的缓冲溶液中20～26小时，然后过滤除水，在真空下，55～65℃干燥10～14小时；(2)然后把步骤(1)的产物碾磨成小于600目的粉末，在碾磨过程中，添加含氨基或脲基的硅烷型偶联剂，即可获得所述的改性碳酸钙。
【技术特征摘要】
1.改性碳酸钙的制备方法，其特征在于，包括如下步骤：(1)将碳酸钙粉末浸渍于弱碱性的缓冲溶液中20～26小时，然后过滤除水，在真空下，55～65℃干燥10～14小时；(2)然后把步骤(1)的产物碾磨成小于600目的粉末，在碾磨过程中，添加含氨基或脲基的硅烷型偶联剂，即可获得所述的改性碳酸钙。2.根据权利要求1所述的方法，其特征在于，所述的弱碱性的缓冲溶液为硼砂-硼酸体系，pH为7.5～8.5。3.根据权利要求1或2所述的方法，其特征在于，所述的硅烷型偶联剂的添加量为0.01～0.02mol/Kg碳酸钙粉末。4.根据权利要求1～3任一项所述方法制备的改性碳酸钙的应用，其特征在于，作为添加剂，用于制备...
【专利技术属性】
技术研发人员：卢晟，郑皓，
申请(专利权)人：上海氯碱化工股份有限公司，
类型：发明
国别省市：上海,31