The present invention relates to an abrasion resistant aging polycaprolactone composite material and a preparation method thereof, by weight consists of the following components: polycaprolactone 60 copies of 80 copies, 16 copies of 20 copies of potassium titanate whisker toughening agent, 6 10 copies, 0.1 copies of the 0.3 light stabilizer, antioxidant 0.1 0.5. The main effect of potassium titanate whisker has two: it has very high hardness, enhance the wear resistance of polycaprolactone. After the coupling agent of titanate whiskers and polycaprolactone compatibility better, improve the enhancement effect of potassium titanate whisker on polycaprolactone, enhances the tensile strength of polycaprolactone; two benzophenone can be used as UV absorbers, enhance the PCL aging property; the invention of polycaprolactone composite the material preparation process is simple and has great popularization value.
【技术实现步骤摘要】
一种耐磨耐老化聚己内酯复合材料及其制备方法
本专利技术属于高分子材料
，特别是指一种耐磨耐老化聚己内酯复合材料及其制备方法。
技术介绍
聚己内酯是一种综合性能优良的工程塑料，其尺寸稳定性好,绝缘性佳，耐油,成型加工性能比较好，但是其耐磨、耐老化性能一般,这大大限制了聚己内酯复合材料在一些特殊材料领域上的应用。如何提高聚己内酯的性能是本领域一直在探索的课题，申请人通过多种的努力，在提高聚己内酯的耐磨性能及耐老化性能方面，获得了较大的进步。
技术实现思路
本专利技术的目的是提供一种耐磨耐老化聚己内酯复合材料及其制备方法，以解决现有技术中的聚己内酯材料的耐磨性能及耐老化性能不高的问题。本专利技术是通过以下技术方案实现的：一种耐磨耐老化聚己内酯复合材料，按重量份由以下组份组成：所述聚己内酯为线形聚己内酯。所述钛酸钾晶须的直径为0.1-0.3μm。所述钛酸钾晶须是用钛酸酯偶联剂AC-201处理后的钛酸钾晶须。所述增韧剂为POE。所述光稳剂为二苯甲酮。所述抗氧剂为三(2,4-二叔丁基)亚磷酸苯酯、四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯或1,3,5-三甲基...
【技术保护点】
一种耐磨耐老化聚己内酯复合材料，其特征在于，按重量份由以下组份组成：
【技术特征摘要】
1.一种耐磨耐老化聚己内酯复合材料，其特征在于，按重量份由以下组份组成：2.根据权利要求1所述的耐磨耐老化聚己内酯复合材料，其特征在于，所述聚己内酯为线形聚己内酯。3.根据权利要求1所述的耐磨耐老化聚己内酯复合材料，其特征在于，所述钛酸钾晶须的直径为0.1-0.3μm。4.根据权利要求1所述的耐磨耐老化聚己内酯复合材料，其特征在于，所述钛酸钾晶须是用钛酸酯偶联剂AC-201处理后的钛酸钾晶须。5.根据权利要求1所述的耐磨耐老化聚己内酯复合材料，其特征在于，所述增韧剂为POE。6.根据权利要求1所述的耐磨耐老化聚己内酯复合材料，其特征在于，所述光稳剂为二苯甲酮。7.根据权利要求1所述的耐磨耐老化聚己内酯复合材料，其特征在于，所述抗氧剂为三(2,4-二叔丁基)亚磷酸苯酯、四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯或1,3,5-三甲基-2,4,6-(3,5-二叔丁...
【专利技术属性】
技术研发人员：刘凯，徐志海，孙启林，
申请(专利权)人：安徽江淮汽车集团股份有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。