一种高保坍聚羧酸减水剂及其制备方法技术

本发明专利技术公开一种高保坍聚羧酸减水剂及其制备方法，由以下组分及质量百分比含量构成：丙稀酸10‑15％，大单体30‑‑40％，双氧水2‑4％，疏基乙酸1‑2％，过硫酸铵1‑2％，甲基丙稀磺酸钠1‑2％，丙稀酸羟乙酯2‑3％，水为余量；各组分的质量百分比之和为100％。减水率可以达到30％以下，含气量在3％以下，坍落度保留值大于170mm，使得产品的综合性能比较好。

A high slump polycarboxylic acid water reducing agent and its preparation method

The invention discloses a high security collapse polycarboxylate superplasticizer and its preparation method comprises the following components and mass percentage: bingxisuan 10 15%, 30 40% macromonomer, hydrogen peroxide 2 4%, 1 2% mercapto acetic acid, ammonium persulfate 1 2% methacrylic acid sodium 1 2%, C 2 dilute acid hydroxyethyl 3%, water margin; component quality% and 100%. The water reduction rate can be less than 30%, the gas content is below 3%, the slump retention value is more than 170mm, which makes the comprehensive performance of the product better.

【技术实现步骤摘要】
一种高保坍聚羧酸减水剂及其制备方法
本专利技术涉及聚羧酸减水剂领域，具体是一种高保坍聚羧酸减水剂及其制备方法。
技术介绍
混凝土预制构件具有标准化生产、绿色化施工、建筑质量超前控制等优点，是实现建筑工业化的重要途径。近年来，随着住宅产业化的迅速发展，对预制构件的需求量越来越大。混凝土是生产预制构件的关键材料，预制构件混凝土与普通预拌混凝土相比，不需要较大的流动性，但为了加快模板周转，提高生产效率，需要较高的早期强度(24h以内)；另外，预制混凝土胶凝材料用量大、水胶比低、坍落度小，因而需要非常好的触变性，便于振捣和抹面。预制混凝土的配制通常都需要掺入一定量的减水剂，尤其是聚羧酸减水剂起到良好的减水、增强，提高施工性能的作用。而普通聚羧酸减水剂一方面早期强度发展缓慢，导致脱模时间延长，生产效率降低，尤其在低温环境条件下该缺陷更加明显；另一方面普通聚羧酸减水剂配制的混凝土触变性较差，不易浇筑和振捣，而且硬化后容易产生“蜂窝麻面”等质量缺陷。目前混凝土已进入“绿色”、“高性能”时代，相应地对混凝土的原材料、工作性、耐久性、节能环保，以及经济性等提出了更高的要求。聚羧酸减水剂具有低掺量、高减本文档来自技高网...

【技术保护点】
一种高保坍聚羧酸减水剂，其特征在于：由以下组分及质量百分比含量构成：丙稀酸10‑15％，大单体30‑‑40％，双氧水2‑4％，疏基乙酸1‑2％，过硫酸铵1‑2％，甲基丙稀磺酸钠1‑2％，丙稀酸羟乙酯2‑3％，水为余量；各组分的质量百分比之和为100％。

【技术特征摘要】
1.一种高保坍聚羧酸减水剂，其特征在于：由以下组分及质量百分比含量构成：丙稀酸10-15％，大单体30--40％，双氧水2-4％，疏基乙酸1-2％，过硫酸铵1-2％，甲基丙稀磺酸钠1-2％，丙稀酸羟乙酯2-3％，水为余量；各组分的质量百分比之和为100％。2.如权利要求1所述的高保坍聚羧酸减水剂，其特征在于：所述大单体为聚醚大单体和/或酯类大单体。3.一种高保坍聚羧酸减水剂的制备方法，其特征在于：具体步骤如...

【专利技术属性】
技术研发人员：杨春晓，古元峰，赵罡，
申请(专利权)人：芜湖市立泰建筑新材料有限公司，
类型：发明
国别省市：安徽,34