The invention relates to the production field of chemical products, especially in the field of DIPA production. DIPA is an important chemical raw material. The process of DIPA is to add aniline and aluminum powder to the alkylation reactor and heat it with heat conducting oil. With the increase of reaction temperature, aniline is gradually dissolved and slowly react with aluminum powder to form aniline aluminum. When the temperature rose to about 285 DEG C, the pressure rose to 3.2 3.8MPa, reaction lasts about 2h after the end, hydrogen is condensed after cooling by 20m high exhaust pipe emptying; emptying into propylene, the reaction temperature is controlled at 310 DEG C and a pressure control in 4.5MPa, and the reaction of aniline aluminum propylene lasts about 35h, 2 generation, 6 two isopropyl aniline aluminum material; after cooling into the hydrolysis tank, plus soft in the hydrolysis tank, hydrolysis reaction, generating DIPA crude and aluminum hydroxide precipitation, the next step to be refined.
【技术实现步骤摘要】
一种DIPA制备流程烷基化反应
本专利技术涉及化工产品生产领域，尤其是DIPA生产领域。
技术介绍
DIPA是一种重要的化工原料。
技术实现思路
工艺流程将苯胺和铝粉加入烷基化反应釜，然后采用导热油对其进行加热，随着反应温度升高，苯胺逐渐溶解，与铝粉缓慢发生反应，生成苯胺铝。待温度升至约285℃、压力升至3.2-3.8MPa、反应持续约2h后结束，氢气经冷凝降温后通过20m高排气筒排空；放空后通入丙烯，反应温度控制在310℃、压力控制在4.5MPa，苯胺铝与丙烯发生反应持续约35h，生成2，6-二异丙基-苯胺铝；物料冷却后转入水解釜，加软水于水解釜中，发生水解反应，最终生成DIPA粗品及氢氧化铝沉淀，待下一步精制。(2)DIPA产品精制水解后的物料进入分相器，水相和有机相经分相器分离后，有机相先在粗料暂存罐暂存；水相和氢氧化铝进入板框压滤机脱水，滤液回水解釜循环利用，滤饼即为铝泥。粗料暂存塔里的粗料连续打入脱水塔脱水，脱水塔采用导热油进行加热，塔顶采出的水和少量物料经冷凝器冷凝后自流入水解釜回收利用；塔底的物料用泵打入脱轻塔。脱轻塔塔顶脱去的苯胺、DIPA和邻异丙基苯...
【技术保护点】
本专利技术涉及原料成分及配比。
【技术特征摘要】
1.本发明涉及原料成分及配比。2...
【专利技术属性】
技术研发人员：胡天忠，裴红霞，张晓磊，
申请(专利权)人：宁夏海诚电化信息科技有限公司，
类型：发明
国别省市：宁夏,64
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。