The invention discloses a boron nitride fiber and its preparation process and application, which comprises the following steps: raw material after melting, drawing into a precursor fiber, after the low temperature nitriding reaction, high temperature tensile, finally obtain the protective coating, melting, drawing for automatic feeding, continuous drawing. By intermittently melting and drawing wire in the existing technology as automatic feeding and continuous drawing, the diameter of the product is reduced from 12% to less than 7%, and even drawing is uniform.
【技术实现步骤摘要】
一种氮化硼连续纤维及其制备工艺与应用
本专利技术属于无机纤维
,具体涉及一种氮化硼连续纤维及其制备工艺与应用。
技术介绍
随着武器超高声速、长航时和精确制导等技术的发展,导弹在飞行过程中弹体表面所承受的气动加热总量越来越大,为了保证武器气动外形及电磁传输信号正常,对天线罩材料的烧蚀性能、电气性能等均提出了苛刻要求。现有可用的石英陶瓷、石英纤维复合材料、氮化硅陶瓷难以满足2000℃以上的长时间高状态使用要求,现有材料体系中BN纤维增强氮化物复合材料是更高状态下的高温透波材料的最佳候选材料。氮化硼纤维具有耐高温(惰性气氛3000K,氧气气氛1123K)、耐化学腐蚀、介电性能优异、电绝缘性好以及与其它材料界面较好的化学相容性等优异的综合性能,氮化硼纤维复合材料可以用做耐超温烧蚀材料、高温透波材料、电池隔膜材料以及中子吸收材料等。BN纤维增强氮化物复合材料能满足2500℃以上应用环境的需求。“十三五”以来国内多个武器型号对氮化硼纤维增强陶瓷耐高温抗烧蚀透波复合材料提出了迫切需求,希望尽快突破氮化硼连续纤维制备的关键技术,实现规模化制备。国内外氮化硼纤维的研制已经有几 ...
【技术保护点】
一种氮化硼连续纤维的制备工艺,其特征是:包括以下步骤:原料经过熔融、拉丝成前驱纤维,之后进行低温氮化反应,高温热拉伸,最后进行防护涂层得到成品,所述熔融、拉丝为自动投料、连续拉丝。
【技术特征摘要】
1.一种氮化硼连续纤维的制备工艺,其特征是:包括以下步骤:原料经过熔融、拉丝成前驱纤维,之后进行低温氮化反应,高温热拉伸,最后进行防护涂层得到成品,所述熔融、拉丝为自动投料、连续拉丝。2.如权利要求1所述的制备工艺,其特征是:所述原料为氧化硼与稀土的混合物。3.如权利要求1所述的制备工艺,其特征是:所述高温热拉伸为纤维连续式收放丝热处理方式。4.如权利要求1所述的制备工艺,其特征是:所述拉丝为按照玻璃纤维工艺拉制出直径为5-7微米,150-250根/束的前驱纤维,将前驱纤维经合股后成0.5-1.5K的氧化硼束丝,然后将n束所述的氮化硼束丝加捻合股。5.如权利要求1所述的制备工艺,其特征是:所述低温氮化反应中的温度为范围为RT~1000℃,氨气总流量为...
【专利技术属性】
技术研发人员:张铭霞,李勇,齐学礼,栾强,李茹,唐建新,黄健,孙淑敏,
申请(专利权)人:山东工业陶瓷研究设计院有限公司,
类型:发明
国别省市:山东,37