The invention discloses a low cost solar heat absorbing ceramic material, which comprises the following components by weight: 15 to 40 portions of silicon nitride, boron nitride from 15 to 40, 5 to 15 portions of titanium silicide, nickel carbide 5 ~ 15, 5 ~ 12 of chromium oxide, alumina is 5 ~ 12, sodium silicate from 2 to 7, 2 to 5 portions of boron oxide, manganese oxide from 2 to 3. The invention adopts the organic foam impregnation process, the preparation of high temperature oxidation resistance, thermal shock resistance, with a three-dimensional network structure, high surface area and high thermal conductivity ceramic materials heat absorption rate, especially suitable for solar thermal power tower absorber.
【技术实现步骤摘要】
一种低成本太阳能吸热陶瓷材料及其制备方法
本专利技术涉及新能源
，尤其涉及一种低成本太阳能吸热陶瓷材料及其制备方法。
技术介绍
新能源是传统能源之外的各种能源形式，包括太阳能、地热能、海洋能、风能和核聚变能等。太阳能是取之不尽用之不竭的可再生资源，开发和利用太阳能是实现能源供应多元化、保证能源安全的重要途径之一。近年来，在节能减排的政策引导和要求下，我国建筑中太阳能光热技术的应用显著增加，对于太阳能建筑一体化的要求也越来越高。塔式太阳能热发电系统由于聚光比高(200-100KW/m2)、热力循环温度高、热损耗小、系统简单且效率高的特点得到世界各国的重视，是目前各国都在大力研究的先进的大规模太阳能热发电技术，作为塔式太阳能热发电核心的空气吸热器，其中的高温吸热体材料担负着接收太阳聚光能量，以及吸热换热的重要作用，影响着整个热发电系统的稳定性及效率的高低。但是，由于塔式吸热器聚光能流密度不均匀性和不稳定性形成的吸热体局部热斑造成材料热应力破坏、空气流动稳定性差以及耐久性不高等问题，因而需迫切的开发具有抗高温氧化性好、抗热震性好、具有三维或者二维的连通结构、高比表...
【技术保护点】
一种低成本太阳能吸热陶瓷材料，其特征在于，包括以下重量份的组分：氮化硅 15～40份，氮化硼 15～40份，硅化钛5～15份，碳化镍5～15份，氧化铬5～12份，氧化铝5～12份，硅酸钠2～7份，氧化硼2～5份，一氧化锰2～3份。
【技术特征摘要】
1.一种低成本太阳能吸热陶瓷材料，其特征在于，包括以下重量份的组分：氮化硅15～40份，氮化硼15～40份，硅化钛5～15份，碳化镍5～15份，氧化铬5～12份，氧化铝5～12份，硅酸钠2～7份，氧化硼2～5份，一氧化锰2～3份。2.根据权利要求1所述的一种低成本太阳能吸热陶瓷材料，其特征在于，包括以下重量份的组分：氮化硅18～35份，氮化硼20～30份，硅化钛8～12份，碳化镍6～10份，氧化铬7～10份，氧化铝6～9份，硅酸钠3～6份，氧化硼3～4份，一氧化锰2～3份。3.根据权利要求1所述的一种低成本太阳能吸热陶瓷材料，其特征在于，包括以下重量份的组分：氮化硅30份，氮化硼25份，硅化钛10份，碳化镍9份，氧化铬8份，氧化铝7份，硅酸钠5份，氧化硼3份，一氧化锰2份。4.根据权利要求1所述的一种低成本太阳能吸热陶瓷材料，其特征在于，各组分均为平均粒径1～100nm的粉末。5.权利要求1～4中任一项所述一种低成本太阳能吸热陶瓷材料的制备方法，其特征在于，以氮化硅和氮化硼为基材，以硅化钛、碳化镍、氧化铬、氧化铝、硅酸钠、氧化硼以及一氧化锰为添加剂合成耐高温结合相，以聚氨酯泡沫为前驱体，采用有...
【专利技术属性】
技术研发人员：应沛亮，
申请(专利权)人：长兴微羽智能科技有限公司，
类型：发明
国别省市：浙江,33