一种常温还原浸出非洲水钴矿的工艺制造技术

本发明专利技术公开了一种常温还原浸出非洲水钴矿的工艺，包括以下步骤：水钴矿球磨后用水调制成所需的固液比矿浆，加入所需的硫酸，按钴金属量的0.5~1倍的量加入还原剂，反应至所需时间即可完成还原浸出过程；所述还原剂为水合肼和/或羟胺。本发明专利技术的常温还原浸出非洲水钴矿的工艺具有能耗成本低、浸出效率高、工艺简单和成本低廉的特点。

A process for temperature reduction leaching heterogenite Africa

The invention discloses a process for temperature reduction leaching heterogenite in Africa, which comprises the following steps: heterogenite milling water after modulation into the desired ratio of solid to liquid slurry, adding the required sulfuric acid added according to 0.5~1 times the amount of the amount of cobalt metal reducing agent, reaction to the time required to complete the reduction leaching process; the reducing agent for hydrazine hydrate and / or hydroxylamine. The process of the present invention at room temperature reduction leaching heterogenite Africa has the characteristics of energy consumption of low cost, high leaching efficiency, simple process and low cost.

【技术实现步骤摘要】
一种常温还原浸出非洲水钴矿的工艺
本专利技术涉及冶金
，特别是一种常温还原浸出非洲水钴矿的工艺。
技术介绍
目前非洲水钴矿的浸出工艺是用硫酸加还原剂进行还原酸浸：水钴矿经过湿法球磨后，矿浆调整好矿浆比后，加入硫酸在高于70℃下进行酸性还原浸出。由于水钴矿中有部分钴是三价的，不能被硫酸直接浸出。因此在浸出过程中要加入一定量的还原剂。常规加入的还原剂是亚硫酸钠（或焦亚硫酸钠、二氧化硫气体等）。该方法的缺点是：该工艺必须在高温下进行。由于常规的还原剂如亚硫酸钠、焦亚硫酸钠和二氧化硫气体等，其还原能力有限，需要在一定的温度下，才能达到一定的反应速度，满足生产效率的需要。否则其反应时间将大大延长。导致原因：水钴矿中高价的金属主要有Co3+、Mn4+、Fe3+。其标准的氧化还原电位分别是：EoCo3+/Co2+=1.82、EoMnO2/Mn2+=1.23、EoFe3+/Fe2+=0.77。还原剂二氧化硫和羟胺的标准氧化还原电位分别是：Eo（SO4）2-/SO2=0.17、EoN2/NH2OH=-3.04。水合肼与羟胺的相近。从热力学角度来看，二氧化硫和羟胺都可以将矿中的高价金属还原。但动力本文档来自技高网...

【技术保护点】
一种常温还原浸出非洲水钴矿的工艺，其特征在于包括以下步骤：水钴矿球磨后用水调制成所需的固液比矿浆，加入所需的硫酸，按钴金属量质量的0.5～1倍的量加入还原剂，反应至所需时间即可完成还原浸出过程；所述还原剂为水合肼和/或羟胺。

【技术特征摘要】
1.一种常温还原浸出非洲水钴矿的工艺，其特征在于包括以下步骤：水钴矿球磨后用水调制成所需的固液比矿浆，加入所需的硫酸，按钴金属量质量的0.5～1倍的量加入还原剂，反应至所需时间即可完成还原浸出过程；所述还原剂为水合肼和/或羟胺。2.根据权利要求1所述的常温还原浸出非...