耐候性消光粉末涂料及其制备方法技术

本发明专利技术公开了一种耐候性消光粉末涂料，所述耐候性消光粉末涂料由以下质量百分比的组分组成：羟基聚酯树脂混合物56.0‑59.0％，聚氨酯交联剂4.0‑5.0％，流平剂0.8‑1.2％，消泡剂0.40‑0.60％，稳定剂0.40‑0.60％，炭黑0.8‑1.2％，钛白粉32.4‑37.6％。本发明专利技术还公开了一种耐候性消光粉末涂料的制备方法。本发明专利技术的耐候性消光粉末涂料具有生产简单、成本低、重复性好等方面的优点。

Weatherability and extinction powder coatings and their preparation methods

The invention discloses a weather resistant matt powder coatings, the weatherability of extinction powder coating consists of the following components: the mass percentage of hydroxyl polyester resin mixture 56 59%, 4 5% polyurethane crosslinking agent, leveling agent 0.8 1.2%, 0.40 defoaming agent 0.60%, stable agent 0.40 0.60%, carbon black 0.8 1.2%, titanium dioxide 32.4 37.6%. The invention also discloses a preparation method of a weatherproof light powder coating. The weatherproof powder coating of the invention has the advantages of simple production, low cost and good repeatability, etc.

【技术实现步骤摘要】
耐候性消光粉末涂料及其制备方法
本专利技术涉及一种耐候性消光粉末涂料及其制备方法，属于涂料

技术介绍
聚氨酯粉末涂料因优越的耐候性和突出的流平和表面性能成为极佳的选择，广泛用于墙面装饰件、车库门、门窗型材和汽车配件等的涂装。相较于液体涂料，配制消光效果的粉末涂料要困难得多，且制备方法也完全不同。液体涂料中的颜填料在涂膜干燥过程中向表面迁移，这些粒子产生的粗糙度足以形成减光效果。粉末涂料不含溶剂，烘烤过程中熔融粘度相对较高，不存在由低黏度液态向固态的转变，且消光剂在涂膜表面的聚焦很少。因此，急需开发一种生产简单、成本低、重复性好的耐候性消光粉末涂料及其制备方法。
技术实现思路
本专利技术的目的在于提供一种耐候性消光粉末涂料及其制备方法，使耐候性消光粉末涂料具有生产简单、成本低、重复性好等方面的优点。为解决上述技术问题，本专利技术的耐候性消光粉末涂料，所述耐候性消光粉末涂料由以下质量百分比的组分组成：作为本专利技术的改进，所述耐候性消光粉末涂料由以下质量百分比的组分组成：作为本专利技术的改进，所述羟基聚酯树脂混合物由聚酯羟值分别为30和300的羟基聚酯树脂混合而成，聚酯羟值30的羟本文档来自技高网...

【技术保护点】
一种耐候性消光粉末涂料，其特征在于，所述耐候性消光粉末涂料由以下质量百分比的组分组成：

【技术特征摘要】
1.一种耐候性消光粉末涂料，其特征在于，所述耐候性消光粉末涂料由以下质量百分比的组分组成：2.根据权利要求1所述的耐候性消光粉末涂料，其特征在于，所述耐候性消光粉末涂料由以下质量百分比的组分组成：3.根据权利要求1所述的耐候性消光粉末涂料，其特征在于，所述羟基聚酯树脂混合物由聚酯羟值分别为30和300的羟基聚酯树脂混合而成，聚酯羟值30的羟基聚酯树脂与聚酯羟值300的羟基聚酯树脂的重量比为4-6:1。4.根据权利要求3所述的耐候性消光粉末涂料，其特征在于，所述聚酯羟值30的羟基聚酯树脂与聚酯羟值300的羟基聚酯树脂的重量比为5:1。5.根据权利要求1所述的耐候性消光粉末涂料，其特征在于，所述聚氨酯交联剂为缩脲二酮。6.根据权利要求1所述...

【专利技术属性】
技术研发人员：黄立明，刘杨，茅立安，朱晓燕，
申请(专利权)人：浙江明泉工业涂装有限公司，
类型：发明
国别省市：浙江,33