The invention relates to the field of cold mounting film, in particular to a kind of flame retardant acrylic pressure sensitive adhesive for cold mounting film. The cold laminating film is provided with flame retardant acrylic pressure-sensitive adhesive composition by weight percentage: 10 to 17% phosphorus containing acrylic monomer; butyl acrylate methyl methacrylate 42 57%; 8 14% 2 6%; acrylic acid; propylene glycol 4 nitrate 0.1 ~ 0.5%; 10%; 3 ~ 8% melamine curing; agent 3 8% 2 4%; initiator; the phosphorus containing acrylic acid monomer is 2 (ethyl methacrylate methyl) phosphonate, 2 ethyl (methyl acryloyl) phosphonate and 2 (ethyl methacrylate methyl) ester of one or several. Fireproof grade cold laminating film is provided with flame retardant transparent glue flame retardant performance can reach VTM 2; high transparency.
【技术实现步骤摘要】
一种冷裱膜用阻燃丙烯酸酯压敏胶及其制备方法
本专利技术涉及一种压敏胶，特别涉及一种冷裱膜用阻燃丙烯酸酯压敏胶及其制备方法。
技术介绍
压敏胶(PSA)是一类无需借助于溶剂、热或其它手段，只需施加轻度压力，即可与被粘物粘合牢固的胶粘剂。丙烯酸酯类PSA是由丙烯酸酯单体与其它单体共聚而成的。丙烯酸酯类PSA配方简单、粘接范围广、耐候性佳、耐光性强、耐油性优、耐水性好、不存在相分离和迁移等现象，因而在各个领域中应用广泛。丙烯酸酯PSA(与其他碳氢化合物一样)极易燃烧，并且其耐高温性欠佳，故其在某些特殊领域的使用范围受到极大限制。因此，加快对环保阻燃、耐热型丙烯酸酯PSA的开发具有重要意义。CN103275658A提供了一种可剥离型阻燃丙烯酸酯压敏胶的制备方法。虽然这种压敏胶为：将含双键环三磷腈无卤阻燃单体(2-烯丙基苯氧基)五苯氧基环三磷腈(APPCP)与丙烯酸酯类单体进行共聚所制得，其阻燃环保、耐热性能优良，可剥离性能好的。但是这款压敏胶的持粘力、剥离强度和阻燃性的综合性能不佳，耐老化性能一般，在阻燃性较好的情况下，容易失粘。
技术实现思路
为了克服现有的技术不足，本专利...
【技术保护点】
一种冷裱膜用阻燃丙烯酸酯压敏胶，其特征在于，所述冷裱膜用阻燃丙烯酸酯压敏胶按重量百份比组成：含磷丙烯酸单体10‑17％；丙烯酸丁酯42‑57％；甲基丙烯酸甲酯8‑14％；丙烯酸2‑6％；丙烯醇4‑10％；硝酸0.1～0.5％；三聚氰胺3～8％；固化剂3‑8％；引发剂2‑4％；所述含磷丙烯酸单体为2‑乙基(甲基丙烯酸酰氧甲基)膦酸酯、2‑乙基(丙烯酰氧甲基)膦酸酯和2‑乙基(甲基丙烯酸酰氧甲基)磷酸酯中的一种或几种。
【技术特征摘要】
1.一种冷裱膜用阻燃丙烯酸酯压敏胶，其特征在于，所述冷裱膜用阻燃丙烯酸酯压敏胶按重量百份比组成：含磷丙烯酸单体10-17％；丙烯酸丁酯42-57％；甲基丙烯酸甲酯8-14％；丙烯酸2-6％；丙烯醇4-10％；硝酸0.1～0.5％；三聚氰胺3～8％；固化剂3-8％；引发剂2-4％；所述含磷丙烯酸单体为2-乙基(甲基丙烯酸酰氧甲基)膦酸酯、2-乙基(丙烯酰氧甲基)膦酸酯和2-乙基(甲基丙烯酸酰氧甲基)磷酸酯中的一种或几种。2.根据权利要求1所述的冷裱膜用阻燃丙烯酸酯压敏胶，其特征在于：所述含磷丙烯酸单体、三聚氰胺和硝酸的重量比为2-2.5：1：0.03-0.05。3.根据权利要求...
【专利技术属性】
技术研发人员：夏厚君，
申请(专利权)人：浙江欧丽数码喷绘材料有限公司，
类型：发明
国别省市：浙江,33