The invention discloses a PBAT resin and a preparation method thereof, including: (a) terephthalate unit; (b) adipate unit; (c) the total weight of isocyanate; PBAT resin based on the content of isocyanate weight of 0.31% 0.59%. The present invention in the PBAT resin. By adding a small amount of isocyanate, and the isocyanate content at 0.31% 0.59% range, not only can reduce the content of carboxyl terminated polyester chain reaction, and can lead to branched molecular chains in the generation of the cross-linked polymer molecules to a certain extent, the formation of network structure thus, PBAT resin prepared by 95 DEG C boiled for 12 hours after the change of melting rate of less than 15, the relative viscosity change rate of less than 0.22, has significantly improved the boiling water resistance aging performance.
【技术实现步骤摘要】
一种PBAT树脂及其制备方法
本专利技术属于高分子材料合成领域，具体涉及一种具有良好耐水煮老化性的PBAT树脂及其制备方法。
技术介绍
降解聚酯材料已经被广泛应用，如薄膜、发泡材料、注塑制件等。此类材料具有良好的物理性质，并且在堆肥或者自然状态下可以降解为水和二氧化碳，对环境没有潜在危害。其中，聚己二酸对苯二甲酸丁二酯树脂（PBAT）是目前生物降解塑料研究中非常活跃的降解材料之一。然而，此类材料多数是由脂肪族聚酯或者脂肪族/芳香族共聚酯组成，在高温潮湿的环境下耐水解性能不佳，或者在加工的过程中，由于少量水分的存在，而导致材料降解。聚酯树脂的水解降解是由于水分子进攻聚酯分子中的酯键而引起高分子链的断裂，而且聚酯分子链上的端羧基又能加速酯键的水解断裂。因此，通过控制聚酯树脂的端羧基含量，可以改善聚酯材料的水解稳定性。本专利技术经研究惊讶地发现，在PBAT树脂中加入少量的异氰酸酯，并将异氰酸酯的含量控制在一定范围内，可以使制备得到的PBAT树脂具有良好的耐水煮老化性能。
技术实现思路
本专利技术的目的在于提供一种PBAT树脂，该PBAT树脂具有明显改善的耐水煮老化性能。本专...
【技术保护点】
一种PBAT树脂，其特征在于，包括：（a）对苯二甲酸丁二醇酯单元；（b）己二酸丁二醇酯单元；（c）异氰酸酯；其中，基于PBAT树脂的总重量，异氰酸酯的重量含量为0.31%‑0.59%。
【技术特征摘要】
1.一种PBAT树脂，其特征在于，包括：（a）对苯二甲酸丁二醇酯单元；（b）己二酸丁二醇酯单元；（c）异氰酸酯；其中，基于PBAT树脂的总重量，异氰酸酯的重量含量为0.31%-0.59%。2.根据权利要求1所述的一种PBAT树脂，其特征在于，所述异氰酸酯的重量含量测定方法：使用元素分析仪进行测定，将0.1-0.5gPBAT树脂样品在1150℃高温下的氧气环境中经催化氧化使其燃烧分解，生成气体中的非检测气体被去除，被检测的氮气通过吸附柱分离，再使用热导检测器对氮气进行检测，测定出氮元素的含量，并根据氮元素的含量换算成异氰酸酯的含量，其中氦气作为载气和吹扫气，炉温设定为1150℃，每个样品测试三次取算术平均值。3.根据权利要求1所述的一种PBAT树脂，其特征在于，基于PBAT树脂的总重量，异氰酸酯的重量含量为0.35%-0.45%。4.根据权利要求1所述的一种PBAT树脂，其特征在于，基于PBAT树脂的总重量，所述对苯二甲酸丁二醇酯单元的重量含量T%为35wt%-65wt%。5.根据权利要求1-4任一项所述的一种PBAT树脂，其特征在于，所述PBAT树脂经95℃水煮12小时后，熔融指数变化幅度小于15...