The invention discloses a plastic and a preparation method for automobile interior ornament, and relates to the field of chemical and chemical technology. The automotive interior plastic, which comprises the following parts by weight: 25 to 40 portions of polyethylene material, plasticizer 0.5 ~ 1.5, 0.3 ~ 0.8 antioxidant, anti-aging agent 0.5 to 1.5 parts, anti yellowing agent 0.5 ~ 1.5, 0.5 ~ 1.5 lubricant, light stabilizer 0.3 - 0.8; the the poly propylene containing 20% ~ 30% filler in polypropylene, the filler is one or mixture of glass fiber, calcium silicate, calcium carbonate, barium sulfate, talcum powder, mica, the glass fiber length is 12 ~ 25mm. The automotive interior parts of the invention use plastic sound absorption and noise reduction effect better, less or even odorless volatilization.
【技术实现步骤摘要】
汽车内饰件用塑料及其制备方法
本专利技术涉及化学化工
，尤其是一种汽车内饰件用塑料及其制备方法。
技术介绍
近日，汽车承担了全世界65%以上的货运量和80%以上的客运量。人类，尤其是发达国家的人们，已经离不开汽车了。然而汽车的广泛普及造成了能量和资源的过度消耗。减轻车身自重是减少能耗、节约资源的有效手段。于是，汽车塑料件应运而生。汽车内饰系统是汽车车身的重要组成部分，而且内饰系统的设计工作量占到车造型设计工作量的60％以上，远超过汽车外形，是车身最重要的部分之一。汽车内饰塑料件不但减轻了车身重量（一般塑料的比重在0.9-1.5之间，纤维增强复合材料比重也不会超过2.0，而金属材料的比重A3刚为7.6，黄酮为8.4，铝为2.7。因此，应用塑料是减轻车身自重的有效途径），还耐腐蚀（塑料对酸碱盐等抗腐蚀能力大于钢板）、弹性好具有吸收和衰减振动和噪声的能力，可以提高乘坐的舒适性；同时，由于塑料材料给予汽车设计者更多的灵活性，也使汽车的造型更加多样，拼装更加简单。目前塑料在汽车上的用量是越来越大，汽车内饰已基本实现塑料化，内饰件塑料朝着更美观、手感更好、更具有良好的吸...
【技术保护点】
一种汽车内饰件用塑料，其特征在于包括如下重量份的原料：聚乙烯25～40份，增塑剂0.5～1.5 份，抗氧化剂0.3～0.8份，抗老化剂0.5～1.5 份，抗黄变剂0.5～1.5 份，润滑剂0.5～1.5 份，光稳定剂0.3～0.8份；所述聚丙烯为含有20%～30%的填充物的聚丙烯，所述填充物为玻璃纤维、碳酸钙、硅酸钙、硫酸钡、滑石粉、云母的一种或者多种混合物，所述玻璃纤维长为12～25mm。
【技术特征摘要】
1.一种汽车内饰件用塑料，其特征在于包括如下重量份的原料：聚乙烯25～40份，增塑剂0.5～1.5份，抗氧化剂0.3～0.8份，抗老化剂0.5～1.5份，抗黄变剂0.5～1.5份，润滑剂0.5～1.5份，光稳定剂0.3～0.8份；所述聚丙烯为含有20%～30%的填充物的聚丙烯，所述填充物为玻璃纤维、碳酸钙、硅酸钙、硫酸钡、滑石粉、云母的一种或者多种混合物，所述玻璃纤维长为12～25mm。2.根据权利要求1所述的汽车内饰件用塑料，其特征在于：所述抗黄变剂为季戊四醇四(3-月桂基硫代丙酸酯)、4,4'-二(苯基异丙基)二苯胺和四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯的一种或多种混合物。3.根据权利要求1所述的汽车内饰件用塑料，其特征在于：所述抗老化剂为硫代二丙酸双十二烷酯、三（2,4-二叔丁基苯...
【专利技术属性】
技术研发人员：魏斌，
申请(专利权)人：柳州市宝志塑胶金属制品有限公司，
类型：发明
国别省市：广西,45