墙板的制备方法及墙板技术
The preparation method and wall panel of the wall panel
A method for the preparation of a wall panel and a wall board, which belong to the field of building materials. The preparation method includes mixing the raw material and forming the concrete. The raw materials include 77~83 parts of magnesium chloride solution, 69~75 Magnesium Oxide, 5~11 black powder and 22~28 plant powder according to the weight ratio. The concentration of magnesium chloride solution is 20 to 31 DEG B, black powder from fly ash desulfurization, at least one plant from sawdust, straw powder in powder. The preparation method is simple. The wall plate is made by the preparation method, which has high strength, good durability, light quality, convenient handling and installation.
【技术实现步骤摘要】
墙板的制备方法及墙板
本专利技术涉及建筑材料领域，具体而言，涉及一种墙板的制备方法及墙板。
技术介绍
墙板是建筑中常用的隔断用建筑材料。混凝土墙板在住房、工厂车间及库房中均有很好的应用。混凝土墙板具有良好的结构力学性能、明确的传力层次、简洁的几何形状,是一种可制成大跨度、大覆盖面积且比较经济的承载构件，适用性佳。但是，现有技术中的混凝土墙板普遍存在强度不佳、耐久性不佳、质量大、不便于搬运和安装等问题。
技术实现思路
本专利技术的目的在于提供一种墙板的制备方法，其制备方法简单，制得的墙板强度高、耐久性佳、质量轻。本专利技术的另一目的在于提供一种墙板，其强度高、耐久性佳、质量轻、搬运和安装方便。本专利技术的实施例是这样实现的：一种墙板，其包括将原料搅拌得混凝土，成型；原料按重量份计包括氯化镁溶液77～83份、氧化镁69～75份、黑粉5～11份以及植物粉22～28份，氯化镁溶液的浓度为20～31°Bé，黑粉由粉煤灰脱硫得，植物粉选自木屑、农作物秸秆粉中的至少一种。一种墙板，由上述的墙板的制备方法制得。本专利技术实施例的有益效果是：本专利技术实施例提供的墙板的制备方法，操作过...
【技术保护点】
一种墙板的制备方法，其特征在于，包括：将原料搅拌得混凝土，成型；所述原料按重量份计包括氯化镁溶液77～83份、氧化镁69～75份、黑粉5～11份以及植物粉22～28份，所述氯化镁溶液的浓度为20～31°Bé，所述黑粉由粉煤灰脱硫得，所述植物粉选自木屑、农作物秸秆粉中的至少一种。
【技术特征摘要】
1.一种墙板的制备方法，其特征在于，包括：将原料搅拌得混凝土，成型；所述原料按重量份计包括氯化镁溶液77～83份、氧化镁69～75份、黑粉5～11份以及植物粉22～28份，所述氯化镁溶液的浓度为20～31°Bé，所述黑粉由粉煤灰脱硫得，所述植物粉选自木屑、农作物秸秆粉中的至少一种。2.根据权利要求1所述的墙板的制备方法，其特征在于，所述原料按重量份计还包括粉煤灰空心微珠2～6份；可选地，所述原料按重量份计包括所述氯化镁溶液78～82份、所述氧化镁70～74份、所述黑粉6～10份、所述粉煤灰空心微珠3～5份以及植物粉23～27份；可选地，所述原料按重量份计包括所述氯化镁溶液80份、所述氧化镁72份、所述黑粉8份、所述粉煤灰空心微珠4份以及植物粉25份。3.根据权利要求1所述的墙板的制备方法，其特征在于，所述氧化镁的粒度为-100目，所述黑粉的粒度为-200～+300目，所述植物粉的粒度为-16～+30目，所述粉煤灰空心微珠的粒度为-16～+30目。4.根据权利要求1或2任一项所述的墙板的制备方法，其特征在于，所述成型包括成型第一墙体，成型所述第...