A high density of magnesium oxychloride cement concrete and a preparation method thereof, and relates to a cement concrete and a preparation method thereof, according to the weight percentage: Magnesium Oxide (activity 73% 96 6%~10%, 2%~6% Liushuihelvhuamei powder), water 1%~4%, sodium phosphate three 0.1%~0.3%, TEOS 0.05%~0.2%, butyl phosphate three 0.01%~0.03%, filling sand 79.47%~90.84%. According to the method of magnesium oxychloride cement component Liushuihelvhuamei weight will dissolve in water; and mixing evenly; will be uniformly mixed in the mixed solution, magnesium oxychloride cement concrete mix with the abrasive tap; dried at room temperature curing 24h can release. The magnesium oxychloride cement concrete prepared by the invention has the advantages of quick setting and hardening, good water resistance, high strength and high density, which is much higher than that of common magnesium cement, and can meet the needs of many high-density heavy profiles.
【技术实现步骤摘要】
一种大密度型氯氧镁水泥混凝土及其制备方法
本专利技术涉及一种水泥混凝土及其制备方法，特别是涉及一种大密度型氯氧镁水泥混凝土及其制备方法。
技术介绍
氯氧镁水泥是由瑞典学者索瑞尔在1867年专利技术了一种胶凝材料，它由轻烧MgO、MgCl2、和H2O三者按照一定配比调和形成，也称索瑞尔(Sorel)水泥。氯氧镁水泥是一种气硬性胶凝材料，其具有凝结硬化快，弱碱性和低腐蚀性，较好的耐磨性，突出的粘结性，良好的阻燃性，较好的隔热性等优点，具有很好的应用前景，但目前绝大多数的氯氧镁水均用于轻质型材中，而用于特殊用途的大密度型重质型材的研究则较少。加大氯氧镁水泥混凝土的应用方向对氯氧镁水泥混凝土推广使用至关重要。
技术实现思路
本专利技术的目的在于提供一种大密度型氯氧镁水泥混凝土及其制备方法，本专利技术制备的氯氧镁水泥混凝土具有凝结硬化快，耐水性好，强度高，密度比一般镁水泥高了很多倍，能够满足许多大密度重质型材的需求。本专利技术的目的是通过以下技术方案实现的：一种大密度型氯氧镁水泥混凝土，所述混凝土按重量百分比计，其组分为：氧化镁(活性为73%的96粉)6%~10%；六水合氯化镁...
【技术保护点】
一种大密度型氯氧镁水泥混凝土，其特征在于，所述混凝土按重量百分比计，其组分为：氧化镁(活性为73%的96粉)6%~10%；六水合氯化镁2%~6%；水1%~4%；磷酸三钠0.1%~0.3%；正硅酸乙酯0.05%~0.2%；磷酸三丁酯0.01%~0.03%；填料铁砂79.47%~90.84%。
【技术特征摘要】
1.一种大密度型氯氧镁水泥混凝土，其特征在于，所述混凝土按重量百分比计，其组分为：氧化镁(活性为73%的96粉)6%~10%；六水合氯化镁2%~6%；水1%~4%；磷酸三钠0.1%~0.3%；正硅酸乙酯0.05%~0.2%；磷酸三丁酯0.01%~0.03%；填料铁砂79.47%~90.84%。2.根据权利要求1所述的一种大密度型氯氧镁水泥混凝土，其特征在于，氯氧镁水泥混凝土密度为4179~5014kg/m3。3.根据权利要求1所述的一种大密度型氯氧镁水泥混凝土，其特征在于，所述填料为大密度的铁砂。4.根据权利要求1所述的一种大密度型氯氧镁水泥混凝土，其特征在于，所...